Color PEEK R&D Series
PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw material. Having good thermal stability, color consistency, high purity, and high-temperature resistance, our PEEK material colorR&D series is just as high quality as other plastic PEEKmaterialseries.
PEEK Natural ColorR&D Series Specifications
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
||||
If you want to know more about peek material cost, please contact us.
在线联系供应商
Other supplier products
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
 |
Antistatic Material PEEK R&D Series | AntistaticPEEKR & D Series has excellent electrical insulation, high temperature resistance and wear resistance. Anti-static peek color is blac... |
 |
Peek Materials Applications | Peek Material Applications Natural peek materialhas excellent comprehensive properties and can replace traditional materials such as metals and ... |
 |
CA Series-770CA30 PEEK Carbon Fiber Reinforcement | CA Series-770CA30 carbon fiber filled peekreinforcement is widely used in automobile and aviation fields. It is widely used in automobile fuel pump... |
 |
Color PEEK R&D Series | PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw mate... |
Same products
 |
Trimellitic anhydride 97% | 卖方: Yufeng International Group Co., Ltd | Trimellitic anhydrideis a 2-benzofuran compound having oxo groups at the 1- and 3-positions and a... |
 |
Isobutyric Anhydride CAS 97-72-3 | 卖方: Yufeng International Group Co., Ltd | Product Name: Isobutyric Anhydride CAS No.: 97-72-3 Purity: 99% Molecular Formula: C6H10O3 Mo... |
 |
Isobutyric Acid CAS 79-31-2 | 卖方: Yufeng International Group Co., Ltd | Product Name:ISOBUTYRIC ACID Synonyms: 2-Methylpropanoic acid 79-31-2 Isobutanoic acid 2-Met... |
 |
2-Amino-2-methyl-1-propanol（AMP）CAS：124-68-5 | 卖方: Yufeng International Group Co., Ltd | AtYufeng, a trusted 2-Amino-2-methyl-1-propanol Factory & Supplier, we prioritize quality and... |
 |
Dimethyl sulfoxide (DMSO) CAS: 67-68-5 | 卖方: Yufeng International Group Co., Ltd | Yufengis one of the leading dimethyl sulfoxide suppliers and also a professional such manufacture... |