Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAH

Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAH

Hydroxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers

Hydroxyl Modified Vinyl Chloride,Hydroxyl Modified Vinyl Acetate Terpolymers,Hydroxyl Modified Vinyl Chloride Supplier

New grade MVAH: It is white powder、ester soluble with colorless and transparent solution,and it has with excellent solvent release、film-forming、dispersibility、color contrast property and wettability,moreover, it has excellent dispersibility in pigment and has very good adhesive force on PET,which can completely replace Solbin A grade of Nissin and T5HX grade of Kaneka etc.

MVAH Vinyl Resin Quality standard (XHQB-10)

	Item	Index	Test method
1	Appearance	White powder	By visual
2	Whiteness	≥80	GB2913-82
3	Composition % by Wt	Vinyl Chloride 90±1%	GB/T7139-2002
		Vinyl Acetate 3±1%	ISO1159-1978
		Vinyl Alcohol 7±0.5%
4	Reactive Functionality (Hydroxyl %)
5	Hydroxyl Value	70-76	ISO2554-1974
6	K Value	46-48	GB/T 3401-2007
7	Viscosity No. ml/g	52-56	GB/T 3401-2007
8	Glass transition Temp℃	About 79	GB11998-89
9	Average Molecular Wt	About 27000	Calculated by the Viscosity No.
10	% by wt, through 60 mesh	100%	GB/T6003.1
11	Apparent density (g/ml)	≥0.5	GB20022-2005
12	Volatilization (%)	≤1%	GB/T2914-1999
13	Impurity Particle No. /100g	≤20	GB9348-88
14	20% resin in EA or MEK	Colorless and Transparent or Yellowish	By visual

Application:

MVAH new grade is mainly used for application gravure plastics composite printing inks、PU inks、can sealed coatings、plastic coatings、magnetic tape and carbon tape adhesive、car refinishing paint etc.

Package, storage and transportation:

* In kraft bag, lined with pp bags of 25kgs net, with PE inner bag.

* Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and caution against wet.

* Must be transported in clean vehicle with awning and keep away from moisture.

* It is NOT hazardous article, and the shelf life is one year from the production date.

Other supplier products

	羧基改性氯乙烯-醋酸乙烯-马来酸-马来酸酐四元共聚树脂（FVAM）	特性：改性超高分子量氯乙烯-乙烯-马来酸-马来取代四元共聚树脂，具有大致组成为85％氯乙烯，13％醋酸乙烯，1％顺丁稀二酸，1％马来甲醛，平均分子量约27000，K值约46。FVAMA由于含有羧基基团，其对光滑的基材如金属，尤其是铝箔具有优异的附着力。其漆膜同时对PVC，ABS，纸张，织物，混...
	Vinyl Resin For gravure composite printing inks	Vinyl Resin For gravure composite printing inks Good ester solubility, and compatibility with polyurethane resin, the hydroxyl-modified vinyl resin...
	Vinyl Chloride and Vinyl Acetate Copolymers Resins TLC-40/43	Vinyl Chloride and Vinyl Acetate Copolymers Resins TLC-40/43 Vinyl Chloride and Vinyl Acetate Copolymers Vinyl Resin,Vinyl Acetate Copolymer Resi...
	Vinyl Chloride and Vinyl Acetate Copolymers MLC-14-62	Vinyl Chloride and Vinyl Acetate CopolymersMLC-14-62 Vinyl Chloride and Vinyl Acetate Copolymers Vinyl Chloride Copolymer Resin Price,vinyl chlor...
	Vmc Vinyl Resin For Coating	Vmc Vinyl Resin For Coating Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers Vmc Vinyl Resin For Metal Inks,Vmc Vinyl Resin For Uv Surf...

供应产品

Same products

	Spun-Laced Non-woven Fabrics Production Line	卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD	Spun-Laced Non-woven Fabrics Production Line The Spun-Laced Non-woven Fabrics Production Line fr...
	Needle Punched Non-woven Fabrics Production Line	卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD	Needle Punched Non-woven Fabrics Production Line The needle punching machinefrom RIFA is an adva...
	Non-woven Fabric Machine	卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD	NonWoven Fabric Machine RIFA’s nonwoven slitting machineis a groundbreaking addition to th...
	RFJA32 Fiberglass Weaving Machine	卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD	RFJA32 Fiberglass Weaving Machine The RFJA32 Fiberglass Air Jet Loomis a specialized weaving mac...
	RFJAT28 Air Jet Terry Looms	卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD	RFJAT28 Air Jet Terry Looms The RFJAT28 Air Jet Terry Loomis a specialized weaving machine desig...