hydroxyfunctional polyacrylic dispersion (MT-A-145)
Characterization
MT-A-145 is a water-reducible, hydroxyfunctional polyacrylic dispersion.It is suitable for use in combination with aliphatic polyisocyanates to formulate
aqueous two-component clear- and topcoats for vehicle repair applications,heavy transport finishing and industrial coating.
It is also suitable for use in combination with amino resins or blocked polyisocyanates for waterborne, one-component, industrial baking coatings.
Form supplied
Form supplied is approximately 45% in water / solvent naphtha 100 / 2-butoxyethanol, dimethyl ethanol amine neutralized, 4% solvent naphtha 100, 4% 2-butoxyethano.
Solubility / thinnability
Can be thinned with water. It has only partial compatibility
with glycol ethers and glycol ether esters
Compatibility
Suitable co-reactants for the formulation of waterborne two-component polyurethane systems are aliphatic polyisocyanates.
Properties / Applications
General
MT-A-145 is a hydroxyfunctional polyacrylic dispersion which can be thinned with water to application viscosity.
MT-A-145 has good pigment wetting properties and high shear stability. Bead mills have proved suitable as grinding equipment. Only pigments and extenders with a minimal water-soluble content should be used.
Given the many pigments and extenders available, compatibility testing should always be carried out.
Application and formulation equipment can be cleaned with water, alkaline cleaning agents or isopropanol.
Two-component industrial coatings MT-A-145 combined with aliphatic polyisocyanates yields high-gloss topcoats which can be dried at room temperature or force-dried, e.g. at 80°C.
The cured paint films are hard and flexible with good single-coat adhesion and good resistance to solvents and water.
When properly formulated, e.g. in combination with Bayhydur 302 in an NCO/OH ratio of 1.5 : 1, the pot life is approximately 3 hours.
The formulated coating should have a pH between 7.8 and 8.3.
When mixing Bayhydur or Desmodur into the mill base, a thickener must be added to ensure a high shear effect. The addition of approximately 0.3%
One-component industrial baking coatings
MT-A-145 can be used in combination with melamine resins for the formulation of baking coatings with < 5% co-solvent at application viscosity.
The systems cure in as little as 30 minutes at 120°C. The ratio of MT-A-145 to amino resin (solids on solids) is generally 80 : 20. Given the many amino resins available, compatibility testing should always be carried out.
As a hydroxyfunctional binder, Bayhydrol A 145 is also suitable as a co-reactant for waterborne aliphatic polyisocyanates. The OH : NCO ratio should be 1 : 1. To ensure the storage stability of one-component coating systems based on Bayhydrol A 145, the pH should be set to approx. 8.5 during formulation.
As with any product, use of Bayhydrol A 145 in a given application must be tested (including but not limited to field testing) in advance by the user to determine suitability.
Storage
Should be stored in tightly sealed original containers and protected from freezing, heat, and foreign materials. Short-time cooling down to -18°C does not typically damage the product, but the viscosity may increase significantly. Prolonged freezing can damage the product irreversibly. The viscosity of the product is largely governed by the pH. As the pH may decrease during storage, a decrease in viscosity is also to be expected. The viscosity can be restored to its original value by the addition of small amounts of
an aqueous 10% solution of dimethylethanolamine. Prolonged storage at higher temperatures may result in a decrease of viscosity and/or an increase of average particle size, possibly resulting in sedimentation or coagulation.
Recommended storage temperature is greater rthan 0º-30ºC.
Storage time
as a shelf life of six months from date of receipt at customer, provided the material is stored in sealed original containers at the recommended storage temperature.
在线联系供应商
Other supplier products
 |
Epoxy Adhesive | MT 4003/5112/3042/4512LV series and EP242 series: The characteristics of good toughness, wide applicable temperature, and moderate activation time... |
 |
Methyl Isoamyl Ketone (MIAK) CAS 110-12-3 | Introduction Names and Identifiers Name 5-Methyl-2-hexanone Synonyms MIAKIsobutylacetonmethyl-2-hexanone5-Methyl-2-hexanone5-methylh... |
 |
Epoxy resin adhesive | Epoxy Resin Adhesives: Properties and Applications Table 1: Key Properties of Epoxy Resin Adhesives PropertyTypical ValueSignificance ... |
 |
Benzyl Chloride CAS 100-44-7 | Introduction Properties and Applications 1.1 Molecular formula, Molecular weight, Structural formula and CAS No. Molecular formula: C7H7Cl Mole... |
 |
Leveling agent STD-2033 | Composition: Polyether modified silicone oil Appearance: light yellow viscous liquid Active ingredient: 100% Solvent: None Application range: ... |
Same products
 |
Epoxy/Polyester Powder Coatings | 卖方: Standard International Group (HK) Limited | Feature: -Good bond ability and mechanical performance -Smooth and glossy -Certified chemical ... |
 |
Polyester Clear Powder Coatings | 卖方: Standard International Group (HK) Limited | This series of product are made of polyester resin (as hardener) and highly transparentmaterials.... |
 |
Acrylic Clear Powder Coatings | 卖方: Standard International Group (HK) Limited | Feature: -Excellent exterior exposure durability -Excellent durable high gloss -Excellent clar... |
 |
Polyurethane Powder Coatings | 卖方: Standard International Group (HK) Limited | Feature： -Excellent exterior exposure durability -Good flowing -Excellent chemical resistance ... |
 |
MDF Powder Coating | 卖方: Standard International Group (HK) Limited | Feature： -Environmental friendly -No solvents and volatile organic compounds involved which are... |