Foam Repeated Compression Tester
Get a quote：
Whats/App: +86 181 0160 0864
Web: gellowen.co.uk
Foam repeated compression testing machine will accurately measure the thickness of the test piece, placed in the compression plate of the testing machine, at the rate of 60 times per minute, compress the specimen at the frequency of 60 times to compress the height of the specimen 50%, reciprocating compression up to 80.000 times, after 30 minutes at room temperature, measure its thickness to convert the compression deformation rate.
Applications
1. Applicable Foam Material Types
Polyethylene foam materials (corresponding standards: ISO 7214. JIS K6767)
Latex foam rubber cushioning materials (corresponding standard: JIS K6382)
Other flexible porous polymer foams (such as polyurethane soft foam, etc., adaptable to similar compression fatigue testing requirements)
2. Applicable Product Fields
Furniture industry: Foam cushions for sofas/chairs, backrest foam, mattress filling foam (testing for collapse and deformation after long-term use)
Automotive interior industry: Car seat cushioning foam, headrest foam, interior shock-absorbing foam (evaluating performance stability after repeated compression during driving)
Packaging industry: Foam materials for cushioning packaging (verifying protective capabilities after multiple compressions)
Daily necessities industry: Foam cushions, footrests, and other products (testing durability during daily use)
Standards
GB/T 40872-2021: Test Methods for Polyethylene Foams
ISO 7214:2007: Cellular plastics — Polyethylene — Test methods
JIS K6382: Test Method for Repeated Compression of Rubber Materials
GB/T 42258-2022: Determination of Fatigue Properties of Flexible Porous Polymer Materials by Constant Deformation Method
JIS K6767-1999: Test Methods for Polyethylene Foams and Cellular Rubber Materials
Features
1. Standardized Testing Functions and Procedures
The system simulates the repeated compression conditions of foam materials in actual use. The sample is compressed to 50% of its initial height at a frequency of 60 cycles/minute, allowing for up to 80.000 cycles of reciprocating compression.
After testing, the sample is left to rest at room temperature for 30 minutes before precisely measuring its thickness and calculating the compression deformation rate. The process conforms to professional testing standards and effectively evaluates the fatigue resistance of the foam. The system possesses precise sample thickness measurement capabilities, providing fundamental support for the accuracy of the test data.
2. Multi-Standard Compatibility
Compliant with international standard ISO 7214 (Test Methods for Polyethylene Foam Materials), Japanese Industrial Standard JIS K6767 (Polyethylene Foam Testing), and JIS K6382 (Latex Foam Rubber Cushioning Material Testing), it meets the compliance testing needs of different types of foam materials.
3. Flexible Technical Adaptability
The compression stroke covers 0-50mm, adaptable to foam samples of various thicknesses (such as common 20-50mm thick samples). Equipped with a stable operating system (such as a motor and LCD counter), it supports high-cycle (up to 80.000 cycles) continuous reciprocating compression. The testing process does not require long-term personnel supervision, and the system automatically stops after reaching the set number of cycles.
Technical Parameters
| Parameter | Specification |
|---|---|
| Meet the standard | ISO-7214. JIS-K6767. K6382 |
| Compression stroke | 0——50mm |
| Compression rate | 60 cpm (cycles per minute; noted: original shows "60cm", likely a typo) |
| Pressure plate spacing | 200mm |
| Test size | 200×200mm |
| Plate area | 30×30cm |
| Upper pressure plate | V-type exhaust trench distance: 19×19mm |
| Lower pressure disc | 289 air holes, hole distance: 19mm |
| Motor | 1/3HP |
| Counter | LCD, 0——999999 |
| Volume | 60×40×75cm |
| Weight | 102kg |
| Power Supply | 1 # AC 220V, 5A (noted: original shows "AC220. 5A", corrected for clarity) |
在线联系供应商
Other supplier products
 |
Load-Controlled Friction and Wear Testing Machine | Get a quote： Whats/App: +86 181 0160 0864 Web: gellowen.co.uk The Load-Controlled Friction and Wear Testing Machine is designed for comprehensiv... |
 |
Suga GX25 | GX25 is designed to artificially reproduce indoor deterioration factors such as sunlight,temperature and humidity.GX25 exposes materials to these... |
 |
DSC Differential Scanning Calorimeter / Differential Scanning Calorimeters | The Differential Scanning Calorimeter (DSC) measures the heat flow to or from a sample under controlled heating conditions. A small amount of sampl... |
 |
True Body Weight Ingress Egress Tester | Get a quote： Whats/App: +86 181 0160 0864 The True Body Weight Ingress/Egress Tester is a specialized machine designed to evaluate either a compl... |
 |
Guarded Heat Flow Meter | Get a quote： Whats/App: +86 181 0160 0864 Web: gellowen.co.uk The Guarded Heat Flow Meter is a precision instrument designed to measure the ther... |
Same products
 |
Resistance Loop Bands | 卖方: Shanghai Pisces Sporting & Leisure Products Co., Ltd | Resistance Loop Bandsare versatile fitness tools designed to enhance muscle strength, flexibility... |
 |
不锈钢焊剂芯焊丝 E308T1-1 E308HT1-1 E308LT1-1 用于304不锈钢焊接的气保焊丝 | 卖方: 863048 | 产品描述 不锈钢药芯焊丝 E308T1-1 E308HT1-1 E308LT1-1，FCAW不锈钢焊丝，AWS A5.22药芯焊丝，304不锈钢焊接耗材，低碳不锈钢药芯焊丝，耐高温不锈钢焊丝，... |
 |
E317LT1-1 焊剂芯线 CO2 不锈钢焊剂含量70% 直径1.0/1.2/1.6mm OEM定制 1200℃熔点 | 卖方: 863048 | 迅卓不锈钢药心焊丝 E317LT1-1 分类： Сварочная проволока E317LT1-1 с флюсом, нержавеющая сталь, 70% содержан... |
 |
Mini Jewelry Laser Repair System – 60W to 400W Precision Welding | 卖方: Beijing JCZ Technology Co., Ltd | The Mini Jewelry Laser Welding Machineis an advanced mini laser welding system engineered for pre... |
 |
Portable Backpack Laser Cleaning Machine – Lightweight, Efficient Rust & Paint Removal | 卖方: Beijing JCZ Technology Co., Ltd | TheHCP-M SeriesBackpack Laser Cleaning Machinefeatures a compact pulsed fiber laser system, desig... |