ZG-P-420/ZG-I-218
Characteristic: High resilience, low density
Application: Applicable to the production of insole for sports shoes and leather shoes.
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-420 |
White or pale yellow, liquid, no foreign material |
18 |
||
|
ZG-I-218 |
Transparent liquid, no foreign material |
20 |
Reference shipments ratio: A/B=31/22 (barrel)
Catalysts and auxiliary agents:
ZG-P-420/ZG-AC-2/water =18kg/220g/80g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/46-50 |
Molded density of sole（g/cm3） |
|
|
Material temperature（℃） |
material: 35-42; B material:38-42 |
Hardness (type A) |
20~40 |
|
Cream time（s） |
6~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
30~45 |
Elongation（％） |
350~450 |
|
Metal mold temperature（℃） |
45~55 |
NBS abrasion resistance（％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature)(40,000 gap length mm) |
＜8 |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
在线联系供应商
Other supplier products
 |
China Medium Hardness Sole PU Resin | ZG-P-5005/ZG-I-5320 Medium and high-density PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high densit... |
 |
ZG-P-5050/ZG-I-5002 | ZG-P-5050/ZG-I-5002,Low-Hardness Shoe Sole PU Resin,Sandals Shoes Sole PU Resin Low-Hardness Shoe Sole PU Resin Sandals Shoes Sole PU Resin Medium ... |
 |
ZG-P-6570H/ZG-I-7118 | ZG-P-6570H/ZG-I-7118 PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high density Application: Applicab... |
|
|
ZG-P-5005/ZG-I-5320 | ZG-P-5005/ZG-I-5320,China Medium Hardness Sole PU Resin,Children Shoes Sole PU Resin China Medium Hardness Sole PU Resin Children Shoes Sole PU Res... |
 |
ZG-P-420/ZG-I-218 | Characteristic: High resilience, low density Application: Applicable to the production of insole for sports shoes and leather shoes. Typi... |