ZG-P-6687/ZG-I-5002
Q/ZHTY 01—2010
Characteristic: High hardness, medium and high density good resilience
Application: Applicable to the production of low-speed type
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-6687 |
Milky,liquid, no foreign materia |
---- |
18 |
|
|
ZG-I-5002 |
Transparentliquid, no foreignmaterial |
---- |
20 |
Catalysts and auxiliary agents
ZG-P-6687/ZG-AC-2/water =18kg/220-320g/30-60g/
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties
|
Reactivity |
Technical index |
Test item |
Reference physicalproperties |
|
Reference ratioP+C/I |
100/110~112 |
Molded density of sole（g/cm3） |
|
|
Material temperature（℃） |
material:45-50 B material:38-42 |
Hardness (type C) |
80~90 |
|
Cream time（s） |
6~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
Elongation（％） |
250~350 |
|
|
Metal mold temperature（℃） |
50~60 |
NBS abrasion resistance（％） |
|
|
Demould time（min） |
Free foam density（g/cm3） |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
在线联系供应商
Other supplier products
 |
ZG-P-5090/ZG-I-5320 | ZG-P-5090/ZG-I-5320 High-hardness and medium and high-density PU Resin for shoe sole of woman high-heeled shoes Characteristic: High hardness, me... |
 |
ZG-P-3450/ZG-I-7249 | ZG-P-3450/ZG-I-7249,Low-Hardness Shoe Sole PU Resin Manufacturer,Low Density Shoe Sole PU Resin Low-Hardness Shoe Sole PU Resin Manufacturer Low De... |
 |
ZG-P-6570H/ZG-I-7118 | ZG-P-6570H/ZG-I-7118 PU Resin for shoe sole with the upper Characteristic: Medium and low hardness, medium and high density Application: Applicab... |
 |
High Density Upper Sole PU Resin | ZG-P-8755/ZG-I-7118 Q/ZHTY 01—2013 Application: Low hardness, high density. Characteristic: Suitable for shoes production. Typical properti... |
 |
ZG-P-5080/ZG-I-5002 | Q/ZHTY 01—2013 Application: High hardness, high density. Characteristic: Suitable for female high-heeled shoes production Typical prop... |