ZG-P-6570H/ZG-I-7118
ZG-P-6570H/ZG-I-7118,,
PU Resin for shoe sole with the upper
Characteristic: Medium and low hardness, medium and high density
Application: Applicable to the production of shoe sole with the upper for men and women
Typical properties of PU Resin
|
Name of products |
Appearance |
Viscosity（Pa·s/50℃） |
Density（g/cm3/40℃） |
Package（kg） |
|
ZG-P-6570H |
White or pale yellow, liquid, no foreign material |
------ |
18 |
|
|
ZG-I-7118 |
Transparent liquid, no foreign material |
------ |
20 |
Reference shipments ratio: A/B=29/24 (barrel)
Catalysts and auxiliary agents:
ZG-P-6570/ZG-AC-2/water =18kg/260g/10-35g/0~400g
Note: corresponding adjustment should be made to the addition of auxiliary agent at different areas, different environment and different production conditions.
Molding conditions & physical properties:
|
Reactivity |
Technical index |
Test item |
Reference physical properties |
|
Reference ratioP+C/I |
100/68-70 |
Molded density of sole（g/cm3） |
|
|
Material temperature（℃） |
material: 45-50; B material:38-42 |
Hardness (type A) |
55~65 |
|
Cream time（s） |
6~9 |
Tensile strength（MPa） |
|
|
Rise time（s） |
30~45 |
Elongation（％） |
350~450 |
|
Metal mold temperature（℃） |
45~55 |
NBS abrasion resistance（％） |
≥10% |
|
Demould time（min） |
Free foam density（g/cm3） |
||
|
Folding endurance (room temperature) (40,000 gap length mm) |
＜8 |
Matching ratio is based on the optimal matching value which will vary with the category and additive amount of paint additives added.
Free foam density will vary with the seasons (temperature, humidity).
Stripping time will be extended with the increase of the thickness of moldings.
Folding endurance conditions: bending angle is 90 degrees and the frequency is 80 times / min * 40 thousand times
Data listed above is just for reference. The specific data is subjected to the practical operation. If other physical properties are required, please contact us.
More information can view .
在线联系供应商
Other supplier products
 |
ZG-P-5080/ZG-I-5220 | ZG-P-5080/ZG-I-5220,Sole PU Resin For High-Heeled Shoes,Medium-Density Shoe Sole PU Resin Sole PU Resin For High-Heeled Shoes Medium-Density Shoe S... |
|
|
ZG-P-6955 / ZG-I-8308 | ZG-P-6955 / ZG-I-8308,PU Resin For Casual Shoes,High Density Low Hardness Sole Pu PU Resin For Casual Shoes High Density Low Hardness Sole Pu Low-h... |
 |
ZG-P-6570/ZG-I-5012 | ZG-P-6570/ZG-I-5012,, Dual density PU Resin for labor protection shoes (safety shoe) sole Characteristic: Medium and low hardness, medium and hig... |
 |
ZG-P-6570/ZG-I-5012 | ZG-P-6570/ZG-I-5012 Dual density PU Resin for labor protection shoes (safety shoe) sole Characteristic: Medium and low hardness, medium and high ... |
 |
Low Hardness Sole PU Resin Supplier | PU Resin for Auto Parts Characteristic: Medium and low hardness, medium density Characteristic: Applicable to the production of related auto ... |