Color PEEK R&D Series
PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw material. Having good thermal stability, color consistency, high purity, and high-temperature resistance, our PEEK material colorR&D series is just as high quality as other naturalPEEK materialseries.
PEEK Material Color R&D Series Specifications
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
More types of peek composite material, please visit our website.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
Natural PEEK Raw Material Applications | Natural PEEK Plastic Applications PEEK polyetheretherketone raw material has excellent comprehensive properties and can replace traditional materi... |
 |
Peek Materials Applications | Peek Material Applications Natural peek materialhas excellent comprehensive properties and can replace traditional materials such as metals and ... |
 |
Grade G PEEK Pure Resin Pellets | With good toughness and impact resistance, Grade G peek pelletscan be disinfected using steam, ethvi alcohol and rays, etc. You can see the wide us... |
 |
CA Series-330CA30 PEEK Carbon Fiber Reinforcement | CA Series-330CA30 peek fccarbon fiber reinforcement is suitable for the production of bushing seals and other products, can be faster from the bear... |
 |
Grade CA Carbon Fiber Reinforcement PEEK | PEEK-CA series reinforced plastics filled with carbon fiber, high elastic modulus, mechanical strength, creep resistance, wear resistance and dynam... |
Похожие товары
 |
Oxytetracycline Hydrochloride Soluble Powder 50% 200g | Продавец: Hebei Shengxue Dacheng Pharmaceutical Co., Ltd. | Oxytetracycline Hydrochloride Soluble Powder is a broad-spectrum antibiotic used to treat a varie... |
 |
Anti-mold for Furniture | Продавец: KOBSO (CHINA) LIMITED | Anti Molds for Cabinet As a experienced supplier in this field for over 10+ years, Kobso Multi-f... |
 |
Anti-mold for Clothes | Продавец: KOBSO (CHINA) LIMITED | In the clothes industry, most of the fabrics, especially natural fabrics, are prone to mold. Base... |
 |
Anti-mold Desiccant | Продавец: KOBSO (CHINA) LIMITED | Anti-mold desiccants are materials used to absorb moisture and prevent mold growth in products an... |
 |
Activated Carbon Desiccant | Продавец: KOBSO (CHINA) LIMITED | Activated Carbon Desiccant The role of activated carbon depends on its own adsorption function, w... |