PA66 GF15 With High Tensile Strength (A2307C, A2317C) for Engineering Plastics
PA66GF15is a 15% glass fiber reinforced, toughened, polyamide 66 resin for injection molding
Typical Application of Anmei GroupPA66 GF15 With High Tensile Strength (A2307C)
PA66 15% glass fiber and high toughness modified grades are applied to the sectors of electrical switch with high tensile characteristics.
Processing Detail of PA66GF15With High Tensile Strength (A2307C)
Other Details of PA66 GF15 With High Tensile Strength (A2307C)
|
Physical Property |
|
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1180Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.7-1.0 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(1.0-1.4% I ISO294-4) |
|
Mechanical Properties |
|
|
Tensile strength (105.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.6% I ISO527) Conditioned |
5mm/ min |
|
Notched Impact Strength (10.0 KJ/m2 I ISO179) Conditioned |
|
|
Flexural Strength (177MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (5050 MPa I ISO178) Conditioned |
2mm/min |
|
Thermal Property |
|
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(225*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
|
Injection Molding Conditions |
|
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！
If you want to know more about pa66 gf15 material properties, please visit our website.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics | Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20halogenated FR. ... |
 |
Transparent ABS (MABS Plastic) for Engineering Plastics | Transparent ABS (MABS Plastic) for Engineering Plastics Transparent ABS, also called MABS plastic material, which has excellent transparency, impa... |
 |
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics | Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20 halogenated FR ... |
 |
PA6 GF45 (A1011I) for Engineering Plastics | Polyamide 6 reinforced with 45% Glass Fibers that is PA6 GF45, medium viscosity and dimensional stability, the PA GF45has excellent rigidity and hi... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. Typical Application of pa6 6 gf30Heat Stabilized (A2006... |
Похожие товары
 |
Defoamer Powder | Продавец: Shandong Jufu Chemical Technology Co., Ltd. | Antifoaming agent powder primarily serves as an essential component in cement and concrete produc... |
 |
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA66 is nylon 66, namely pa66_gf35is glass fiber. Generally expressed as PA66 GF35, that is, 35% ... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, forinjection moulding. PA66GF3... |
 |
PA66 GF30 Halogen-free FR (A2015F) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Material PA66 GF30FR is a PA66 with 30% glass-fibers and flame retardant free of halogens. This t... |
 |
PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA66GF30FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated. Typical Applic... |