PA66 GF15 With High Tensile Strength (A2307C, A2317C) for Engineering Plastics
PA66GF15is a 15% glass fiber reinforced, toughened, polyamide 66 resin for injection molding
Typical Application of Anmei GroupPA66 GF15 With High Tensile Strength (A2307C)
PA66 15% glass fiber and high toughness modified grades are applied to the sectors of electrical switch with high tensile characteristics.
Processing Detail of PA66GF15With High Tensile Strength (A2307C)
Other Details of PA66 GF15 With High Tensile Strength (A2307C)
|
Physical Property |
|
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1180Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.7-1.0 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(1.0-1.4% I ISO294-4) |
|
Mechanical Properties |
|
|
Tensile strength (105.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.6% I ISO527) Conditioned |
5mm/ min |
|
Notched Impact Strength (10.0 KJ/m2 I ISO179) Conditioned |
|
|
Flexural Strength (177MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (5050 MPa I ISO178) Conditioned |
2mm/min |
|
Thermal Property |
|
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(225*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
|
Injection Molding Conditions |
|
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation！
If you want to know more about pa66 gf15 material properties, please visit our website.
Send product request
Other supplier products
 |
PA66 GF30 (A2000F, A2011F, A2111F) | PA6630GFis a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness... |
 |
Anmei-Polyamide Nylon 66 (PA66) for Engineering Plastics | Nylon 66 is polyamide 66. The main purpose of Nylon 66 plastic modification is to improve the properties of Nylon 66 material based on the original... |
 |
Anmei-ABS Engineering Plastic | ABS resin is a terpolymer composed of acrylonitrile, butadiene and styrene. ABS has the rigidity, chemical resistance and heat resistance of polyac... |
 |
PA6 GF20 Heat Stabilized (A1006D, A1016D) for Engineering Plastics | PA6 GF 20has 20% glass fiber filler. It has much greater heat-resistant mechanical properties than unfilled polyamide. Anmeiplastics has always bee... |
 |
Anti-mold Masterbatch for Engineering Plastics | Anmei, one of the professional plastic master batch manufacturers, has a range of customized masterbatches available which incorporate antistatic m... |
Same products
 |
Defoamer Powder | Seller: Shandong Jufu Chemical Technology Co., Ltd. | Antifoaming agent powder primarily serves as an essential component in cement and concrete produc... |
 |
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66 is nylon 66, namely pa66_gf35is glass fiber. Generally expressed as PA66 GF35, that is, 35% ... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, forinjection moulding. PA66GF3... |
 |
PA66 GF30 Halogen-free FR (A2015F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Material PA66 GF30FR is a PA66 with 30% glass-fibers and flame retardant free of halogens. This t... |
 |
PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66GF30FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated. Typical Applic... |