PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics
PA6 15GFwith high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding.
Typical Application of PA6 GF15 with high tensile strength (A1307C)
PA6 with 15% glass fiber toughened plastics, due to its excellent properties, good appearance and easy processing characteristics, which has been successfully applied to the electrical field such as switches, controllers, the auto field such as heat dissipation barriers, accumulator shells, coolant pots, and the mechanical filed such as electric drill and motor housing, pump impeller, pulley, tool handle and bearing.
Other Details of PA6 GF15 with high tensile strength (A1307C)
Physical Property
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1180Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
|
Tensile strength(115.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break(2.0% I ISO527) Conditioned |
|
|
Notched Impact Strength(125 0MPa I ISO527) Conditioned |
2mm/min |
|
Flexural Strength(175MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus(5250 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
|
Melting Point |
(220°C I ISO11357) |
|
Hot Deformation Temperature |
(175*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
240-260°C |
|
Nozzle Temperature |
240-260*C |
|
Tooling Temperature |
80*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
Suzhou ANMEIMaterial Technology Co., Ltd. – the professional supplier of engineering plastic and the color masterbatchwas founded in 2013, which is located in Tongli - the millennium ancient town, 50km far away from Shanghai, the location is very convenient for transportation.
As a modified plastics inc, we will do our best to meet all the needs of customers.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
|
|
PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics | PA6 15GFwith high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding. Typical Applicatio... |
 |
PA6 GF in Anmei | As an engineered plastics company, Anmei focuses on the production of modified engineering plastics, among which high-performance nylon 6 engineeri... |
 |
Color Masterbatch | As one ofmasterbatch suppliers, Anmei serves customers with tailored-making solutions from standard colors to customized colors and functions. Ther... |
 |
Anmei-ABS Engineering Plastic | ABSresin is a terpolymer composed of acrylonitrile, butadiene and styrene. ABS has the rigidity, chemical resistance and heat resistance of polyacr... |
 |
Color Masterbatch for Engineering Plastics | As one of plastic colorant suppliers, Anmei serves customers with tailored-making solutions from standard colors to customized colors and functions... |
Похожие товары
 |
Medical Plastic Parts | Продавец: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | Продавец: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | Продавец: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |