PA66 GF30 (A2000F, A2011F, A2111F)
PA6630GFis a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness, high-temperature resistance and easy forming.
Typical Application of PA66BGF30(A1000F)
The mechanical strength, creep resistance and fatigue strength of 30% reinforced Nylon66 gf30are greatly improved, and the elongation, mold shrinkage, moisture absorption, and wear resistance are reduced. It can be injection-molded plastic parts with stressed structures in the fields of automobiles, E & E, home appliances and machinery industries.
Processing Detail of PA66 GF30 (A1000F)
Other Details of PA66 GF30 (A1000F)
Physical Property
|
Ash |
(30.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1365Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.2-0.5 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.6-0.9% I ISO294-4) |
Mechanical Properties
|
Tensile strength (186.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.4% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (12.5 KJ/m2 IISO179) Conditioned |
|
|
Flexural Strength (282MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (8518 MPa I ISO178) Conditioned |
2mm/ min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(250*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
As a professional engineering plastic supplier, Anmei provide synthetic polymers, material pa66 gf30, pa4 6 gf30, heat stabilized nylon and etc. Want to know pa66 gf30 price? Contact us.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
|
|
PA66 GF30 (A2000F, A2011F, A2111F) | PA6630GFis a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | PA66 GF15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection molding. PA66 GF15 Storage and Handling PRE-PROCESS... |
 |
Antibacterial Masterbatch | Polymer antibacterial masterbatchis a kind ofmasterbatch materialthat adds antibacterial agents into the carrier resin, which is offering antimicro... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, forinjection moulding. PA66GF30is a common nylon material known for its high str... |
 |
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics | Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20halogenated FR. ... |
Похожие товары
 |
Medical Plastic Parts | Продавец: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | Продавец: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | Продавец: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |