PA66 GF30 (A2000F, A2011F, A2111F)

PA6630GFis a polyamide 66 reinforced with 30% glass fibers. It demonstrates outstanding mechanical properties such as high fluidity, high toughness, high-temperature resistance and easy forming.

Typical Application of PA66BGF30(A1000F)

The mechanical strength, creep resistance and fatigue strength of 30% reinforced Nylon66 gf30are greatly improved, and the elongation, mold shrinkage, moisture absorption, and wear resistance are reduced. It can be injection-molded plastic parts with stressed structures in the fields of automobiles, E & E, home appliances and machinery industries.

Processing Detail of PA66 GF30 (A1000F)

Other Details of PA66 GF30 (A1000F)

Physical Property

Ash

(30.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1365Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.2-0.5 % 1 ISO294-4)

Shrinkage Vertical Flow

(0.6-0.9% I ISO294-4)

Mechanical Properties

Tensile strength (186.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.4% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (12.5 KJ/m2 IISO179)

Conditioned

Flexural Strength (282MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (8518 MPa I ISO178)

Conditioned

2mm/ min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(250*C I ISO75)

Conditioned

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

280-300°C

Nozzle Temperature

280-300*C

Tooling Temperature

80-100*C

* Molding conditions arejustfor reference, please make an adjustment based on the actual situation!

As a professional engineering plastic supplier, Anmei provide synthetic polymers, material pa66 gf30, pa4 6 gf30, heat stabilized nylon and etc. Want to know pa66 gf30 price? Contact us.



在线联系供应商

至: Suzhou Anmei Material Technology Co., Ltd
Your E-mail:
消息正文:


Send to other suppliers

Other supplier products

Anti-mold Masterbatch
Anti-mold Masterbatch Antiblock masterbatchfor Engineering Plastics Anmei, one of the professionalplastic master batch manufacturers, has a range of customized masterba...
Color Masterbatch
Color Masterbatch Color Masterbatch As one ofengineering plastic manufacturers, Anmei serves customers with tailored-making solutions from standard colors to cust...
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics PA66 is nylon 66, namely polyamide 66. GF is glass fiber. Generally expressed as pa6 6gf35, that is, 35% glass fiber is added to nylon 66. Typic...
PA66 GF
PA66 GF Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodified products with propertiesof heat-resistant, rei...
PA66 GF50(A2011J)
PA66 GF50(A2011J) PA 66 GF 50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various process...
供应产品

Same products

Medical Plastic Parts
Medical Plastic Parts 卖方: Packson Mold Co.,Ltd Project Management To be a qualified medical plastic components manufacturer, the most advanced ...
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics 卖方: Suzhou Anmei Material Technology Co., Ltd PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol...
PA66 GF
PA66 GF 卖方: Suzhou Anmei Material Technology Co., Ltd Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif...
Nylon6 PA6
Nylon6 PA6 卖方: Suzhou Anmei Material Technology Co., Ltd Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o...
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics 卖方: Suzhou Anmei Material Technology Co., Ltd Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a...