PA66 GF50(A2011J)
PA 66 GF 50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products.
Typical Application of PA66GF50(A2011J)
PA66 50%GF HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings.
Other Details of PA66 50GF(A2011J)
Physical Property
|
Ash |
(50.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1538Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.1-0.3 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
Mechanical Properties
|
Tensile strength (217.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.5% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (17.0KJ/m2 I ISO179 Conditioned |
|
|
Flexural Strength (354 MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (14263 MPa I ISO178) Conditioned |
2mm/ min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(260*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
290-310°C |
|
Nozzle Temperature |
290-310*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
As a professional engineered plastics company, Anmei provide modified polyolefin, pa 6.6 gf50, heat stabilized nylon and etc. Want to know more? Contact us.
Отправить запрос, связаться с поставщиком
Другие товары поставщика
 |
PA6 GF | Anmei-PA6 GF for Engineering Plastics As an engineered plastics company, Anmei focuses on the production of modified engineering plastics, among... |
 |
PA66 GF45 (A2011I) | PA66 GF45is a 45% glass fiber reinforced polyamide 6.6 with high stiffness and strength. Typical Application of PA66 GF45(A2011I) PA66 45%GF HB... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. Typical Application of pa6 6 gf30Heat Stabilized (A2006... |
 |
PA66 GF20 With High Tensile Strength (A2307D, A2317D) for Engineering Plastics | Elastomer toughened nylon 66 with 20% glass fiber is called PA66 GF20, it shows high oil resistance, high impact resistance, good resistance to low... |
 |
Engineering Plastic Application for Different Industries | Engineering Plastic Applicationfor Different Industries Anmei, one of the most experienced engineering plastic andmasterbatch producers, offers ... |
Похожие товары
 |
Medical Plastic Parts | Продавец: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | Продавец: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | Продавец: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Продавец: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |