PA66 GF50(A2011J)
PA 66 GF 50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products.
Typical Application of PA66GF50(A2011J)
PA66 50%GF HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings.
Other Details of PA66 50GF(A2011J)
Physical Property
|
Ash |
(50.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1538Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.1-0.3 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
Mechanical Properties
|
Tensile strength (217.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.5% I ISO527) Conditioned |
5mm/min |
|
Notched Impact Strength (17.0KJ/m2 I ISO179 Conditioned |
|
|
Flexural Strength (354 MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (14263 MPa I ISO178) Conditioned |
2mm/ min |
Thermal Property
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(260*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
290-310°C |
|
Nozzle Temperature |
290-310*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
As a professional engineered plastics company, Anmei provide modified polyolefin, pa 6.6 gf50, heat stabilized nylon and etc. Want to know more? Contact us.
在线联系供应商
Other supplier products
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | Why Nylon Has High Tensile Strength Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics UsingPolyamide 66as ... |
 |
Anmei-TPU Flame Retardant for Engineering Plastics | Anmei-TPU Flame Retardant for Engineering Plastics TPU thermoplastic polyurethane elastomer is a type of polyurethane elastomer. It not only has t... |
 |
PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics | PA6 GF15with high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding. Typical Applicatio... |
 |
Color Masterbatch for Engineering Plastics | Color Masterbatch for Engineering Plastics As an engineering plastic company, Anmei serves customers with tailored-making solutions from standard ... |
 |
Anti-mold Masterbatch | Anmei,a professionalplastic masterbatch company, has a range of customized masterbatches available which incorporate conductive masterbatch, antist... |
Same products
 |
Medical Plastic Parts | 卖方: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | 卖方: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | 卖方: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |