PA 66 GF 50is a fiber-reinforced plastic made of Nylon 66 resin as a base material and 50% glass fiber as a reinforcing filler, and various processing aids be added to be used in injection molding products.

Typical Application of PA66GF50(A2011J)

PA66 50%GF HB grade is applied to the field of industrial product structural parts, requiring high strength, high toughness, high and low-temperature resistance, and commonly used as water valve diverter and blade of air outlet, mechanical gears and bushings.

Other Details of PA66 50GF(A2011J)

Physical Property

Ash

(50.0% 1 ISO3451/1)

Conditioned

600°C*2h

Density

(1538Kg/m3 1 ISO1183)

Conditioned

23°C

Shrinkage Parallel Flow

(0.1-0.3 % 1 ISO294-4)

Shrinkage Vertical Flow

Mechanical Properties

Tensile strength (217.0MPa 1 ISO527)

Conditioned

5mm/ min

Tensile Strain at Break (2.5% I ISO527)

Conditioned

5mm/min

Notched Impact Strength (17.0KJ/m2 I ISO179

Conditioned

Flexural Strength (354 MPa 1ISO178)

Conditioned

2mm/min

Flexural Modulus (14263 MPa I ISO178)

Conditioned

2mm/ min

Thermal Property

Melting Point

(260°C I ISO11357)

Hot Deformation Temperature

(260*C I ISO75)

Conditioned

Flammability Class

(HB 1UL94)

Conditioned

mm

Injection Molding Conditions

Drying Temperature

130°C

Drying Time

3h

Cylinder Temperature

290-310°C

Nozzle Temperature

290-310*C

Tooling Temperature

80-100*C

* Molding conditions arejustfor reference, please make an adjustment based on the actual situation!

As a professional engineered plastics company, Anmei provide modified polyolefin, pa 6.6 gf50, heat stabilized nylon and etc. Want to know more? Contact us.



Send product request

To: Suzhou Anmei Material Technology Co., Ltd
Your E-mail:
Message text:


Send to other suppliers

Other supplier products

Color Masterbatch for Engineering Plastics
Color Masterbatch for Engineering Plastics Color Masterbatch for Engineering Plastics As an engineering plastic company, Anmei serves customers with tailored-making solutions from standard ...
Masterbatch
Masterbatch We are here to be your reliable partners of Color Masterbatch. Color masterbatches are widely used in polyethylene(PE), polypropylene(PP), polysty...
Low-shrinkage PBT Masterbatch for Engineering Plastics
Low-shrinkage PBT Masterbatch for Engineering Plastics Tubes are colored to make the identification process easier in loose tube optical fiber cables. Low-shrinkage PBT masterbatchmaterial as loose tube...
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20 halogenated FR ...
Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics
Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics Flame-retardant PA66FRis a halogen-free flame retardant engineering plastic made of nylon 66 resin as a base material (other fibers can also be add...
All supplier products

Same products

Medical Plastic Parts
Medical Plastic Parts Seller: Packson Mold Co.,Ltd Project Management To be a qualified medical plastic components manufacturer, the most advanced ...
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics Seller: Suzhou Anmei Material Technology Co., Ltd PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol...
PA66 GF
PA66 GF Seller: Suzhou Anmei Material Technology Co., Ltd Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif...
Nylon6 PA6
Nylon6 PA6 Seller: Suzhou Anmei Material Technology Co., Ltd Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o...
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics Seller: Suzhou Anmei Material Technology Co., Ltd Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a...