Degassing Flux(SATA-PF-350)
General Description of Degassing Flux (SATA-PF-350)
Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux is a kind of traditional high efficiency aluminum degassing fluxand its alloys, it used for removing hydrogen and oxides from the aluminium melting.
Application of Degassing Flux (SATA-PF-350)
Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.
Advantage of Degassing Flux (SATA-PF-350)
Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
It has excellent performance in refining, degassing and drossing
It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min
Specification of Degassing Flux (SATA-PF-350)
White mixed powder
It is suit for all series alloy except high magnesium alloy,
Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
Working Temperature: 710℃-780℃
Package of Degassing Flux (SATA-PF-350)
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.
NOTE: This flux has serious hygroscopicity, please use immediately after opening.
Send product request
Other supplier products
 |
Reclaimed Fluxes | General Description of Reclaimed Fluxes Reclaimed fluxes is a strongly exothermic flux and used as covering and drossing flux, recovery of grindin... |
 |
Mg Alloy Flux | Magnesium alloyfluxhas a low melting point and small heat capacity. When heated in the air, it gets oxidized fast, and it is easy to burn when over... |
 |
Granulated Fused Refining Fluxes | General Introduction: SATA is a eutectic salt composed of mgcl2 anhydrous and potassium or sodium chloride. Which can removes alkali metal(sodium, ... |
 |
WELCOME JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Jinzhou SATA Fused Fluxes and New Materials is the professionally leading manufacturer of foundry fluxes and chemicals, serving the foundry industr... |
 |
Fluxes for Aluminum Alloy | General Introduction: SATA granular shaped fluxis a eutectic salt composed of mgcl2 anhydrous and potassium or sodium chloride. Which can removes a... |