General Description of Degassing Flux (SATA-PF-350)
Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux is a kind of traditional high efficiency aluminum degassing fluxand its alloys, it used for removing hydrogen and oxides from the aluminium melting.
Application of Degassing Flux (SATA-PF-350)
Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.
Advantage of Degassing Flux (SATA-PF-350)
Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
It has excellent performance in refining, degassing and drossing
It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min
Specification of Degassing Flux (SATA-PF-350)
White mixed powder
It is suit for all series alloy except high magnesium alloy,
Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
Working Temperature: 710℃-780℃
Package of Degassing Flux (SATA-PF-350)
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.
NOTE: This flux has serious hygroscopicity, please use immediately after opening.
在线联系供应商
Other supplier products
 |
Magnesium Chloride Granule | General Introduction: Chemical formular: Mgcl2 6H2O Purity: 46.00%min. Appearance: pure white crystal power CAS NO.:7791-18-6 Chemically, is repr... |
 |
Fluxes for Magnesium Alloy | Magnesium alloy has a low melting point and small heat capacity. When heated in the air, it gets oxidized fast, and it is easy to burn when overhea... |
 |
Grain Refiner | Grain Refiner General Description of Grain Refiner Grain refiner can optimize the form and grain distribution of eutectic silicon. The material syn... |
 |
Potassium Aluminum Fluoride (PAF) | General Description of Potassium Aluminum Fluoride (PAF) It is also called Potassium Cryolite, Potassium Tetrafluoraluminate, Kalium Aluminium Flu... |
 |
Sodium free refining flux | General Description: Aluminum alloys containing more than 2 % magnesium become brittle with sodium. Sodium free refining fluxFeature: This flux is ... |