PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics
PA66 is nylon 66, namely pa66_gf35is glass fiber. Generally expressed as PA66 GF35, that is, 35% glass fiber is added to nylon 66.
Typical Application of PA66 GF35(A2000G)
It is applied to lamp holder cover and cooling fan, gears and various electronic connectors, wear-resistant parts of elevators, and internal and external structural parts around the engine such as cooling fan.
Processing Detail of PA66GF35(A2000G)
Other Details of PA6.6 GF35(A2000G)
|
Physical Property |
|
|
Ash |
(35.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1407Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.2-0.4 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.5-0.8% I ISO294-4) |
|
Mechanical Properties |
|
|
Tensile strength (105.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break (2.6% I ISO527) Conditioned |
5mm/ min |
|
Notched Impact Strength (10.0 KJ/m2 I ISO179) Conditioned |
|
|
Flexural Strength (177MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus (5050 MPa I ISO178) Conditioned |
2mm/min |
|
Thermal Property |
|
|
Melting Point |
(260°C I ISO11357) |
|
Hot Deformation Temperature |
(255*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
|
Injection Molding Conditions |
|
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
280-300°C |
|
Nozzle Temperature |
280-300*C |
|
Tooling Temperature |
80-100*C |
* Molding conditions are just for reference, please make an adjustment based on the actual situation!
As a reliable plastics engineering company, we will do our best to meet all the needs of customers.
Want To Buy High-quality PA material as Engineering PlasticMasterbatch? Come to Anmei, a professional engineering plastic/masterbatch company!
Send product request
Other supplier products
 |
Anmei-PA66 GF for Engineering Plastics | Anmeifocuses on the production of modified engineering plastics. We have polyamide PA66 modified products with propertiesof heat-resistant, rein... |
 |
PA6 GF15 With High Tensile Strength (A1307C, A1317C) for Engineering Plastics | PA6 15GFwith high tensile strength is made by 15% glass fiber reinforced, toughened, polyamide 6 resin for injection molding. Typical Applicatio... |
 |
Low-shrinkage PBT Masterbatch for Engineering Plastics | Tubes are colored to make the identification process easier in loose tube optical fiber cables. Low-shrinkage PBT masterbatchmaterial as loose tube... |
 |
PA6 GF30 Halogen-free FR (A1015F) for Engineering Plastics | PA6 FRis a PA6 with 30% glass-fibers and flame retardant free of halogens. Typical Application of PA6 GF30 halogen-free FR (A1015F) PA6 GF30f... |
 |
PA66 GF20 Halogenated FR (A2014D, A2114D) for Engineering Plastics | Nylon 66, filled with 20% of glass fiber and flame resistance halogens, are extruded by Coperion twin-screw extruder is PA66 GF20 halogenated FR ... |
Same products
 |
Defoamer Powder | Seller: Shandong Jufu Chemical Technology Co., Ltd. | Antifoaming agent powder primarily serves as an essential component in cement and concrete produc... |
|
|
PA66 GF35 (A2000G, A2011G, A2111G) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66 is nylon 66, namely pa66_gf35is glass fiber. Generally expressed as PA66 GF35, that is, 35% ... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, forinjection moulding. PA66GF3... |
 |
PA66 GF30 Halogen-free FR (A2015F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | Material PA66 GF30FR is a PA66 with 30% glass-fibers and flame retardant free of halogens. This t... |
 |
PA66 GF30 Halogenated FR (A2014F, A2114F) for Engineering Plastics | Seller: Suzhou Anmei Material Technology Co., Ltd | PA66GF30FR is a Nylon 66 with 30% glass-fibers and flame retardant halogenated. Typical Applic... |