Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02

During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects.

 

The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ferrules, if the process is not proper, the cracks may be directly caused or the hidden cracks may be buried for the occurrence of the lap ring grinding cracks.

 

There are many ways to form cracks in bearing rings: Raw material defects include: cracks in raw materials and the effects of raw material defects on the grinding process.

 

Forging defects include forging cracks, effects of forged microstructure defects on the grinding process, and cutter cracks. There are also various heat treatment defects and the like. Therefore, crack detection and hardness testing are essential. BKN has considerable experience in crack detection, and Bearing Ring Crack and Hardness Combination crack testing equipment is a perfect combination.

 

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 Brief Introduction

Detection process

 

Vibrating plate and string charging →hardness test→crack detection→automatic blanking

 

Bad product sorting

 

Automatic charging —automatic detection—automatic sorting —automatic blanking

 

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02.jpg

 

Charging mechanism

 

Bearing Ring-Crack and Hardness Combination Flaw Detector TQJC-02.jpg

 

Hardness testing

 

Bearing Ring Crack and Hardness-Combination Flaw Detector TQJC-02.jpg

 

Crack detection(the probe uses stainless steel casing+nano abrasion material ) to ensure long-term normal of the probe

 

 

 

Bearing Ring Crack and Hardness Combination-Flaw Detector TQJC-02.jpg

 

Discharging sequencing mechanism

 

Crack sensitivity: a crack with a depth of ≥0.05 mm and a length of ≥1 mm extending inward from the surface of the ferrule; for a crack that has not extended to the surface inside the ferrule, when the thickness between the subcutaneous surface and the surface of the workpiece is ≤0.2 mm, the depth is ≥0.20 mm Cracks of length ≥ 1 mm can be detected.

 

Hardness sensitivity: Rockwell 1HRC ~ 2HRC (other parameters remain stable and consistent).

Eddy Current Testing Equipment

ECT Eddy current testing is a non-contact testing method, which mainly uses the electromagnetic field and electromagnetic induction between metals to detect. It is one of the NDT non-destructive testing methods in the industry.

 

Why BKN NDT Testing Equipment

 

The technology of BKN originated from eddy current Laboratory of Institute of Materials, Nanjing University of Technology. At present, it is a leading high-tech non destructive testing equipment suppliers in China. The company is committed to the development of eddy current, ultrasonic, magnetic flux leakage and various non-standard equipment, holding independent research and development of a number of national patents.

 



Send product request

To: Nanjing BKN Automation System Co.,LTD
Your E-mail:
Message text:


Send to other suppliers

Other supplier products

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all d...
MFL101 Tank Floor MFL Scanner
MFL101 Tank Floor MFL Scanner Technical Characteristics of MFL101 Tank Floor MFL Scanner The mfl scannerhas a unique full modular structure, from the main body of the compute...
BKNET-0102 Welded Pipe Eddy Current Flaw Detector
BKNET-0102 Welded Pipe Eddy Current Flaw Detector The technology of BKN originated from eddy current Laboratory of Institute of Materials, Nanjing University of Technology. At present, it is a lead...
Steel Bar Testing
Steel Bar Testing The steel bar is rolled by a rolling mill and produce both surface defects and internal defects during the rolling process. The internal defect is ...
MFL-7389 Tube Magnetic Flux Leakage Detector
MFL-7389 Tube Magnetic Flux Leakage Detector Tubing repair is an important measure to reduce the comprehensive cost of production in oil production plants to improve the quality of repairing t...
All supplier products

Same products

LM-79 Moving Detector Goniophotometer (Mirror Type C)
LM-79 Moving Detector Goniophotometer (Mirror Type C) Seller: LISUN ELECTRONICS (SHANGHAI) CO.,LTD Measurement:Luminous Intensity Data, Photometric Data, Luminous Intensity Distribution, Zonal Lum...
HB Series
HB Series Seller: Shanghai Kinglos Musical Instruments Co., Ltd. Personalized Violin Violin with carving flower, your personalized violin. Top: spruce. Back/Side...
Beginner Violin
Beginner Violin Seller: Shanghai Kinglos Musical Instruments Co., Ltd. Good Beginner Violin Face material: Solid Spruce Back / Side: Maple Fingerboard material: ...
Advance Series
Advance Series Seller: Shanghai Kinglos Musical Instruments Co., Ltd. Professional Violin Professional performance violin with high cost performance. Maple texture...
Acoustic Violin
Acoustic Violin Seller: Shanghai Kinglos Musical Instruments Co., Ltd. The semi acoustic violinproduced by kinglos have good quality, many varieties and complete specif...