Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAF
Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAF
Hydroxyl Modified Vinyl Chloride,Hydroxyl Modified Vinyl Acetate Terpolymers,Hydroxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers
New grade MVAF: It is white powder、ester soluble with colorless and transparent solution, and it has with excellent solvent release、film-forming、dispersibility、color contrast property and wettability, moreover, it has excellent dispersibility in pigment and has very good adhesive force on PET,which can completely replace T5HX grade of Kaneka etc.
MVAF Vinyl Resin Quality standard (XHQB-10)
Item |
Index |
Test method |
|
1 |
Appearance |
White powder |
By visual |
2 |
Whiteness |
≥80 |
GB2913-82 |
3 |
Composition % by Wt |
Vinyl Chloride 84±1% |
GB/T7139-2002 |
Vinyl Acetate 14±1% |
ISO1159-1978 |
||
Hydroxylalkyl Acrylate 2±0.5% |
|||
4 |
Reactive Functionality (Hydroxyl %) |
||
5 |
Hydroxyl Value |
70-76 |
ISO2554-1974 |
6 |
K Value |
46-48 |
GB/T 3401-2007 |
7 |
Viscosity No. ml/g |
52-56 |
GB/T 3401-2007 |
8 |
Glass transition Temp℃ |
About 79 |
GB11998-89 |
9 |
Average Molecular Wt |
About 27000 |
Calculated by the Viscosity No. |
10 |
% by wt, through 60 mesh |
100% |
GB/T6003.1 |
11 |
Apparent density (g/ml) |
≥0.5 |
GB20022-2005 |
12 |
Volatilization (%) |
≤1% |
GB/T2914-1999 |
13 |
Impurity Particle No. /100g |
≤20 |
GB9348-88 |
14 |
20% resin in EA or MEK |
Colorless and Transparent |
By visual |
Application:
MVAF new grade is mainly used for application gravure plastics composite printing inks、PU inks、can sealed coatings、plastic coatings、magnetic tape and carbon tape adhesive etc.
Package, storage and transportation:
* In kraft bag, lined with pp bags of 25kgs net, with PE inner bag.
* Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and caution against wet.
*Must be transported in clean vehicle with awning and keep away from moisture.
* It is NOT hazardous article, and the shelf life is one year from the production date.
Send product request
Other supplier products
Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Copolymers VMA | Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Copolymers VMA Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers Ink Raw Material Vinyl C... | |
HVAMA | HVAMA Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers Vinyl Chloride/Vinyl Acetate Copolymers,Vinyl Chloride/Vinyl Acetate Copolymer R... | |
Vinyl Chloride and Vinyl Acetate Copolymers MLC-10-80 | Vinyl Chloride and Vinyl Acetate Copolymers MLC-10-80 Vinyl Chloride and Vinyl Acetate Copolymers Vinyl Acetate Copolymers Resins,Vinyl Chloride ... | |
Vinyl Chloride and Vinyl Acetate Copolymers MLC-14-62 | Vinyl Chloride and Vinyl Acetate CopolymersMLC-14-62 Vinyl Chloride and Vinyl Acetate Copolymers Vinyl Chloride Copolymer Resin Price,vinyl chlor... | |
Vinyl Chloride and Vinyl Acetate Copolymers Resins TLC-40/43 | Vinyl Chloride and Vinyl Acetate Copolymers Resins TLC-40/43 Vinyl Chloride and Vinyl Acetate Copolymers Vinyl Resin,Vinyl Acetate Copolymer Resi... |
Same products
Spun-Laced Non-woven Fabrics Production Line | Seller: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | Spun-Laced Non-woven Fabrics Production Line The Spun-Laced Non-woven Fabrics Production Line fr... | |
Needle Punched Non-woven Fabrics Production Line | Seller: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | Needle Punched Non-woven Fabrics Production Line The needle punching machinefrom RIFA is an adva... | |
Non-woven Fabric Machine | Seller: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | NonWoven Fabric Machine RIFA’s nonwoven slitting machineis a groundbreaking addition to th... | |
RFJA32 Fiberglass Weaving Machine | Seller: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | RFJA32 Fiberglass Weaving Machine The RFJA32 Fiberglass Air Jet Loomis a specialized weaving mac... | |
RFJAT28 Air Jet Terry Looms | Seller: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | RFJAT28 Air Jet Terry Looms The RFJAT28 Air Jet Terry Loomis a specialized weaving machine desig... |