Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAF
Hydroxyl Modified Vinyl Chloride/Vinyl Acetate Terpolymers MVAF
Hydroxyl Modified Vinyl Chloride,Hydroxyl Modified Vinyl Acetate Terpolymers,Hydroxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymers
New grade MVAF: It is white powder、ester soluble with colorless and transparent solution, and it has with excellent solvent release、film-forming、dispersibility、color contrast property and wettability, moreover, it has excellent dispersibility in pigment and has very good adhesive force on PET,which can completely replace T5HX grade of Kaneka etc.
MVAF Vinyl Resin Quality standard (XHQB-10)
|
Item |
Index |
Test method |
|
|
1 |
Appearance |
White powder |
By visual |
|
2 |
Whiteness |
≥80 |
GB2913-82 |
|
3 |
Composition % by Wt |
Vinyl Chloride 84±1% |
GB/T7139-2002 |
|
Vinyl Acetate 14±1% |
ISO1159-1978 |
||
|
Hydroxylalkyl Acrylate 2±0.5% |
|||
|
4 |
Reactive Functionality (Hydroxyl %) |
||
|
5 |
Hydroxyl Value |
70-76 |
ISO2554-1974 |
|
6 |
K Value |
46-48 |
GB/T 3401-2007 |
|
7 |
Viscosity No. ml/g |
52-56 |
GB/T 3401-2007 |
|
8 |
Glass transition Temp℃ |
About 79 |
GB11998-89 |
|
9 |
Average Molecular Wt |
About 27000 |
Calculated by the Viscosity No. |
|
10 |
% by wt, through 60 mesh |
100% |
GB/T6003.1 |
|
11 |
Apparent density (g/ml) |
≥0.5 |
GB20022-2005 |
|
12 |
Volatilization (%) |
≤1% |
GB/T2914-1999 |
|
13 |
Impurity Particle No. /100g |
≤20 |
GB9348-88 |
|
14 |
20% resin in EA or MEK |
Colorless and Transparent |
By visual |
Application:
MVAF new grade is mainly used for application gravure plastics composite printing inks、PU inks、can sealed coatings、plastic coatings、magnetic tape and carbon tape adhesive etc.
Package, storage and transportation:
* In kraft bag, lined with pp bags of 25kgs net, with PE inner bag.
* Store in a dry and ventilated place, do not place in open-air, avoid storage in direct sunlight and caution against wet.
*Must be transported in clean vehicle with awning and keep away from moisture.
* It is NOT hazardous article, and the shelf life is one year from the production date.
在线联系供应商
Other supplier products
 |
Vinyl Resin for Food Packaging Ink | Vinyl Resin for Food Packaging Ink Good ester solubility, and compatibility with polyurethane resin, the hydroxyl-modified vinyl resin is steaming ... |
 |
Vinyl Resin for Reflective Ink | Vinyl Resin for Reflective Ink Good dispersibility to the pigments. Carboxyl-Modified Vinyl Chloride/Vinyl Acetate Terpolymersis white powder, ket... |
 |
Vinyl Resin For gravure composite printing inks | Vinyl Resin For gravure composite printing inks Good ester solubility, and compatibility with polyurethane resin, the hydroxyl-modified vinyl resin... |
 |
Vinyl Resin for Heat Transfer Ink | Vinyl Resin for Heat Transfer Ink Good adhesion to PVC and dispersibility to pigments, heat transfer printing temperature can be reduced. It is wh... |
 |
羧基改性氯乙烯-醋酸乙烯-马来酸-马来酸酐四元共聚树脂（FVAM） | 特性：改性超高分子量氯乙烯-乙烯-马来酸-马来取代四元共聚树脂，具有大致组成为85％氯乙烯，13％醋酸乙烯，1％顺丁稀二酸，1％马来甲醛，平均分子量约27000，K值约46。FVAMA由于含有羧基基团，其对光滑的基材如金属，尤其是铝箔具有优异的附着力。其漆膜同时对PVC，ABS，纸张，织物，混... |
Same products
 |
Spun-Laced Non-woven Fabrics Production Line | 卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | Spun-Laced Non-woven Fabrics Production Line The Spun-Laced Non-woven Fabrics Production Line fr... |
 |
Needle Punched Non-woven Fabrics Production Line | 卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | Needle Punched Non-woven Fabrics Production Line The needle punching machinefrom RIFA is an adva... |
 |
Non-woven Fabric Machine | 卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | NonWoven Fabric Machine RIFA’s nonwoven slitting machineis a groundbreaking addition to th... |
 |
RFJA32 Fiberglass Weaving Machine | 卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | RFJA32 Fiberglass Weaving Machine The RFJA32 Fiberglass Air Jet Loomis a specialized weaving mac... |
 |
RFJAT28 Air Jet Terry Looms | 卖方: ZHEJIANG RIFA TEXTILE MACHINERY CO., LTD | RFJAT28 Air Jet Terry Looms The RFJAT28 Air Jet Terry Loomis a specialized weaving machine desig... |