MF-680 Extra Fast Clear Coat
MF-680 Extra Fast Clear Coat.
Automotive Paint company
Product Name/Model:MF-680 Extra Fast Clear Coat.
Characteristic:Extra fast drying clear coate, high gloss and hardness, easy application, lowconsumption and high efficiency to ensure good profit, suitable for fast spots repair.
Substrates |
1K Basecoat. |
||||
Mixing Ratio |
Clear Coat |
Hardener |
Thinner |
||
2 |
1 |
||||
<25℃ |
680 Extra Fast DryingClear Coat |
681 Extra Fast DryHardener |
62 Fast Thinner |
||
SprayViscosity |
14-16s to drop off, in 4# viscosity cup at 25°C, |
||||
Pot-Life |
At 25°C, 1.5 hour. |
||||
Re-Treatment |
There are particlesorruns after spray, sand affected area with P2000 sand paperafter thorough drying, then polish to solve the problem. |
||||
Spray Gun Set Up |
Gravity Feed: 1.2-1.5mm 4-5kg/cm ²Suction Feed: 1.4-1.6mm 4-5kg/cm² |
||||
SprayTechnology |
Coats&Thickness: 2-3 coats, total 25-35umFlash-Off Time: At 25°C, 5-10 minutes between two coats,Air-Drying Time: Allow 10-15 minutes air drying time before force drying |
||||
Drying Time |
Temperature |
Dust Free |
Tack Free |
Dry to Handle |
Dry to Test |
25°C |
15 minutes |
2 hours |
4 hours |
5 days |
|
70°C |
3 minutes |
10 minutes |
15 minutes |
45 minutes |
|
Shelf Life |
2 years in original sealed can, cool and dry place at 20℃. |
||||
Package |
5L×4or2.5L×8or5L+2.5L+1L |
Note:1. This products are extra fast reaction, after mixing clear coat with hardener, just add smallquantity of thinner for spraying, the mixture should be used up within 1 hour.2. The spray viscosity could not be too high, in case of paints defects, such as orange skin.3. This product is suitable for spots repairs, not suitable for overall repair.4. At temperature lower than 8°C, a forced dry by baking is recommended.5. It is recommended to apply at conditions of temperature lower than 25°C and humidity lowerthan 80%, otherwise there will be defects such as blisteringorblushing.6. The products mixed with hardener should be used up soon and can not be restore for futureuse; clean equipments immediately with thinner after application, otherwise it is very difficult tobe cleaned after dry.
Send product request
Other supplier products
BYTF350 Thinner SRA | BYTF350 Thinner SRA Car Paint Thinner Factory Product Name/Model;BYTF350 Thinner SRA Characteristic: An additive helps to achieve an invisble ... | |
BYT100-2K Binder | BYT100-2K Binder BOYET Series Product Name/Model:BYT100-2K Binder Characteristic:Resin solution used as additive for spraying BM2K Solid Color... | |
MF605-Epoxy Primer | MF605-Epoxy Primer Automotive Paint company Product Name/Model:MF605-Epoxy Primer Characteristic: Good fillibility, easy sanding, give excelle... | |
MSD-0925 Retarder Solvent | MSD-0925 Retarder Solvent Car Paint Degreaser Product Name/Model:MSD-0925 Retarder Solvent Characteristic: Additive to prolong volatilization of s... | |
MSD-0910 Degreaser | MSD-0910 Degreaser Automotive Refinish Coatings Product Name/Model:MSD-0910 Degreaser Characteristic: Able to remove greaser, oil and other su... |
Same products
Fast Dry Alkyd Antirust Primer (Iron Red, Gray) | Seller: Tianjin Jinhai Special Coatings & Decoration Co., Ltd | The fast-drying alkyd anti-rust paint is composed of alkyd resin and anti-rust pigments. Its surf... | |
Exterior Wall Paint | Seller: Tianjin Jinhai Special Coatings & Decoration Co., Ltd | Weather Resistant Acrylic Exterior Latex Wall Paint is a premium quality, water based 100% acryli... | |
DRINKING WATER TANK PAINT | Seller: Tianjin Jinhai Special Coatings & Decoration Co., Ltd | Before the 1950s, water tank inside paint on ships worldwide were protected by cement slurry. It ... | |
CHEMICAL PLANT PAINT | Seller: Tianjin Jinhai Special Coatings & Decoration Co., Ltd | The cooling tower is a large-scale reinforced concrete structure, which is mainly composed of a c... | |
CAUSES OF BUBBLES IN EPOXY ZINC-RICH PRIMER COATING | Seller: Tianjin Jinhai Special Coatings & Decoration Co., Ltd | Epoxy zinc primer paintis widely used in industrial anti-corrosion and has excellent corrosion re... |