Ceramic grade calcined and natural talc powder 325 mesh for body and glaze
CALCINED TALC POWDER
Technical Data Sheet
Item number LMME-CAL
Aftere calcined Whiteness ％≥ 95
SiO2 ％≥ 65
MgO ％≥34
CaO ％≤ 0.3
Fe2O3 ％≤ 0.1
Al2O3 ％≤ 0.2
- ℃) ％≤ 6
ACID SOLUBLE CALCIUM ％≤ 0.4
Moisture ％≤ 0.2
Passing through (45µm) ％≥ 98
NATURAL CERAMICS GRADE TALC POWDER
Technical Data Sheet
Item number LMME-CRA
Aftere calcined Whiteness ≥93％
SiO2 ≥61％
MgO ≥31％
CaO ≤0.5％
Fe2O3 ≤0.1％
Al2O3 ≤0.2％
- ℃) ≤ 6％
ACID SOLUBLE CALCIUM ≤0.4％
Moisture ≤0.2％
Passing through (45µm) ≥98％
Feature: high whiteness&brightness and stability at high temperature, but low iron and loss on ignition to allowing the production of blends and bodies free of dark dots , improve workability and avoid cracks.
Ceramic grade talc powder used for manufacturing atomised clay to ceramic tile body and glaze, electro technical porcelain, all kind of industrial, building, daily-use ceramic glaze, waterproof roll, waterproof paint and waterproof balm etc. Product Description: Talc is increasingly being used in the manufacture of art wares, jars, wall and floor tiles. It serves as a non-plastic ceramic material.
The addition of talc in suitable proportions in the body of mixtures for porcelain, jars etc. prevents the crazing (cracking) effect on the glazes. The proportion of talc in the ceramic body may go up to 80%. It is valued for its refractoriness and stability, as well as extremely law shrinkage at high temperature. Talc converts into clino-enstatite at about 1300º C. Between 800ºC to 840ºC, the water molecules are driven off and talc dissociates into enstatite and amorphous silica without undergoing any change in shape, the shrinkage being 0.0005 inch only.
在线联系供应商
Other supplier products
 |
monohydrate and heptahydrate magnesium sulphate/sulfate MgSO4 price | MAGNESIUM SULPHATE HEPTAHYDRATE Test ItemStandard Result Appearance White Crystal Complies Main Content≥% 99.5 99.74 MgO≥% 16.2 16.23 S... |
 |
Agriculture and fertilizer grade brucite granule and powder price | Bruicte Item number MgO SiO2 CaO Fe2O3 Al2O3 L.O.I Size LMME-58BRU58% 8% 5% 2.5% 1% 31% 80-325mesh LMME-60BRU60% 7% 4% 2.0% 1% 31% 80... |
 |
Industrial refractory grade magnesium oxide powder manufacturer | Dead Burned Magnesite (also known as Dead Burnt Magnesite) Dead burned magnesite is widely used as a basic refractory material. It is produced i... |
 |
paint grade precipitated barium sulphate/sulfate powder price with Reach Certificate | Precipitated Barium sulphate(Barium sulfate)with Reach Certificate Specifications: BaSO4: 98.20% Whiteness:96.1% MOISTURE: 0.015 % FE2O3: 0.003% P... |
 |
Water treatment grade brucite powder MgO 64% 62% 60% price | Bruicte Item number MgO SiO2 CaO Fe2O3 Al2O3 L.O.I Size LMME-58BRU58% 8% 5% 2.5% 1% 31% 80-325mesh LMME-60BRU60% 7% 4% 2.0% 1% 31% 80-... |
Same products
 |
Powder coating primer MT-Active EL140N | 卖方: Standard International Group (HK) Limited | WA：+86 132 6275 2056 WEB: std-coatings.com Product Description MT-Active is a powder coating... |
 |
Powder coating primer MT-Active EL193N | 卖方: Standard International Group (HK) Limited | WA：+86 132 6275 2056 WEB: std-coatings.com Product Overview MT-Active is a powder coating pr... |
 |
Powder coating primer MT-Active EL193N | 卖方: Standard International Group (HK) Limited | WA：+86 132 6275 2056 WEB: std-coatings.com Product Overview MT-Active is a powder coating pr... |
 |
Powder coating primer containing zinc MT-PZ ALZ44TH | 卖方: Standard International Group (HK) Limited | WA：+86 132 6275 2056 WEB: std-coatings.com Product Overview MT-PZ ALZ44TH is a high-performa... |
 |
Powder coating primer containing zinc MT-PZ ALZ55N | 卖方: Standard International Group (HK) Limited | WA：+86 132 6275 2056 WEB: std-coatings.com Product Overview MT-PZ ALZ55N is a high-performan... |