Degassing Flux
Degassing Flux(SATA-PF-350)
General Description of Degassing Flux (SATA-PF-350)
Practice has proved that the hydrogen is the main cause of the pores in the aluminium alloy, the pores not only reduce the actual cross-sectional area of the casting, but also the source of the crack, so it is important part that removing the hydrogen during the smelting process.
SATA-degassing flux also name aluminum degassing fluxisa kind of traditional high efficiency degassing flux for aluminium and its alloys, it used for removing hydrogen and oxides from the aluminium melting.
Application of Degassing Flux (SATA-PF-350)
Plunge suitable quantity flux to the bottom (100mm from the bottom is better) of the melt, evenly and slowly remove the lunch, make the flux fully react with aluminium molten, stand or stir the molten for 10-15 min, the hydrogen and oxide will be taken out of aluminium molten.
Advantage of Degassing Flux (SATA-PF-350)
Easy operation, There are two options. One is with hexachloroethane in tablet form.and another is in powder form without hexachloroethane
It has excellent performance in refining, degassing and drossing
It can enhance the quality of casting, hydrogen content of aluminium molten can reduce to ≤0.1ml/100gAl, the oxide inclusion(Al2O3) can reduce 20% min, the casting inclusion defect reduce 50%min
Specification of Degassing Flux (SATA-PF-350)
White mixed powder
It is suit for all series alloy except high magnesium alloy,
Dosage: recommended dosage: 3%-5% large melting furnace, 4%-6% for crucible furnace
Working Temperature: 710℃-780℃
Package of Degassing Flux (SATA-PF-350)
Packed in 5kg (PE), 25kg (PP), 1000kg bags or customized.
Stored in dry, well-ventilated place, and avoid direct sunlight, keep sealed before using.
NOTE: This flux has serious hygroscopicity, please use immediately after opening.
Send product request
Other supplier products
 |
Magnesium Chloride Anhydrous | Anhydrous magnesium chloride is our main raw materials for producing foundry fluxes, it is a byproduct of titanium sponge from the three largest ti... |
 |
Ceramic Foam Filters | General Introduction: is just developed as a new type molten metal filters to decrease casting flaw in recent years, play a vital role in the metal... |
 |
Anhydrous Magnesium Chloride | Magnesium Chloride Anhydrous (AMC) General Description of Magnesium Chloride Anhydrous (AMC) Name: Magnesium Chloride Anhydrous (AMC) By-product of... |
 |
Alal Alloy Flux | Aluminum is one of the lightest metals in the world. It’s also very strong, extremely flexible and corrosion resistant. Light, durable and fu... |
 |
Magnesium Chloride Granule | General Introduction: Chemical formular: Mgcl2 6H2O Purity: 46.00%min. Appearance: pure white crystal power CAS NO.:7791-18-6 Chemically, is repr... |
Same products
 |
Synthetic Cryolite | Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Synthetic Cryolite General Description ofSynthetic Cryolite Sodium HexafluoroaluminateFormula: Na... |
 |
Sodium Fluosilicate/Hexafluorosilicate (SSF) | Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Sodium Fluosilicate/Hexafluorosilicate (SSF) General Description of Sodium Fluosilicate/Hexafluor... |
 |
Raw Materials | Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Metallurgical flux coating materialrefers to the material which can separate metal from mineral b... |
 |
Mg Alloy Flux | Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Magnesium alloyfluxhas a low melting point and small heat capacity. When heated in the air, it ge... |
 |
Anhydrous Magnesium Chloride | Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY | Magnesium Chloride Anhydrous (AMC) General Description of Magnesium Chloride Anhydrous (AMC) Name... |