Sodium free refining flux

General Description:

Aluminum alloys containing more than 2 % magnesium become brittle with sodium.

Sodium free refining fluxFeature: This flux is a compact covering and cleaning granulated flux to remove the sodium in the aluminum melting. It generates low dust and low fume during application. It reacts quickly with molten aluminum and removes the alkali metal (Ca, Na, Li, Sr) and non-metallic inclusions (oxides, carbides, borides) and degassing.

Function:

After fusing completed the flux are cooled and they are crushed or ground into ccustomerized particle size.

degassing when injected flux with Argon or Nitrogen.

Applied range:

This flux is used in hypo-eutectic aluminum alloys including those contain high magnesium alloy.

Chemical compositions

Mgcl2 Anhydrous , Potassium Chloride , CaF2 and other salt

Melting Point: 432°C & 483°C

Size of Sodium-Free Refining Flux

Granule 0.8-3.25mm, 1-3mm,Other size can be adjusted according to custom

Package: 1. 2.0kg or 2.5kg or 5kg heat sealed polyethylene (PE) bags into 20 or 25kgs bags or cartons with or without pallet

Advantage:

1) Eco‐friendly flux that reduce dust levels, meet the emission limits of most environmental regulatory agencies

2) Uniform size, reacts fully. Purify the melt improve melt quality.

3) Increases the extrusion speed and die life when extruding profiles

4) Reduces the number of breaks in continuous casting

5) Eliminates edge cracks when rolling high Mg aluminium alloys

6) Free of fluorides. Zero fluoride emissions.

7) Low melting point for rapid dispersion

8) Low application rates, typical 0.15-0.2% of MT aluminium

Notice:

Sodium-free flux should be added to the melt at the temperature of 690-750 Degree Celcius. The recommended application rate should be 0.1 to 0.2% of the melt size. Rebel the melt and remove the dross from the top of the molten metal.

Other supplier products

	Degassing Flux	Degassing Flux (SATA-PF-350) General Description of Degassing Flux (SATA-PF-350) Practice has proved that the hydrogen is the main cause of the po...
	Anhydrous Magnesium Chloride	Magnesium Chloride Anhydrous (AMC) General Description of Magnesium Chloride Anhydrous (AMC) Name: Magnesium Chloride Anhydrous (AMC) By-product of...
	Reclaimed Fluxes	General Description of Reclaimed Fluxes Reclaimed fluxes is a strongly exothermic flux and used as covering and drossing flux, recovery of grindin...
	Demag Flux	In some alloys, magnesium is present only as a permitted impurity within limits, and significant amounts may be detrimental. Demag fluxis applicati...
	Fluxes for Aluminum Alloy	General Description: Aluminum alloys containing more than 2 % magnesium become brittle with sodium. Feature: This low sodium refining fluxis a comp...

All supplier products

Same products

	Synthetic Cryolite	Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY	Synthetic Cryolite General Description ofSynthetic Cryolite Sodium HexafluoroaluminateFormula: Na...
	Sodium Fluosilicate/Hexafluorosilicate (SSF)	Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY	Sodium Fluosilicate/Hexafluorosilicate (SSF) General Description of Sodium Fluosilicate/Hexafluor...
	Raw Materials	Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY	Metallurgical flux coating materialrefers to the material which can separate metal from mineral b...
	Mg Alloy Flux	Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY	Magnesium alloyfluxhas a low melting point and small heat capacity. When heated in the air, it ge...
	Anhydrous Magnesium Chloride	Seller: JINZHOU SATA FUSED FLUXES AND NEW MATERIALS FACTORY	Magnesium Chloride Anhydrous (AMC) General Description of Magnesium Chloride Anhydrous (AMC) Name...