45CrNi4Mo/1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings

Product Details

Chemical composition

C	Mn	Si	Cr	V	Mo	P	S
				-		≤0.03	≤0.03

Equivalent grades:

DIN		AFNOR	JIS	BS	SIAU	GB,YB
X45NiCrMo4		Y35NCD16	-	-	-	45CrNi4Mo

Applicationcharacterized by high level harden-ability and toughness. Suitable for the fabrication of tools exposed to repeated impacts and strong pressure in service. Treated for maximum hardness, it can also be used to construct cold work dies for cutlery, jewelry and plastic, anvils for hammers, rams and pile drivers dies and punches for horizontal forging machines rolls for hot work bending machines. It is advisable to use the blocks for dies treated at various hardness limits according to the etching depth complying with the indications given below.

Heat treatment:

Isothermal annealing:

- Heat to 880°C, hold at temperature for 1/2 h to 1 h;

- Furnace cooling to 610°Cand hold at temperature for at least 30 hours;

- Cool by 10°C/h to 580°C;

- Cooling in air.

Following isothermal annealing with sub-critical annealing, holding at temperature for 10-12 hours, maximum. Softening is obtained with HB<270

Stress relieving:

To be carried out after maching and before the final heat treatment.

- Heat to 630°C, hold for 4-6 hours;

- Furnace cooling to 300-350°C;

- Cooling in air.

Hardening:

- Initial preheating to 350-450°C;

- Second preheating to 650-750°C;

- Heat to hardening temperature in the range 850-880°C and hold at temperature;

- Accrording to the shape and dimensions of the tool, cooling in still or forced air, possibly, in oil or in salt bath at 450-500°C;

in the latter case, as soon as the temperature of the tool is even, continue cooling in air.

Quenched hardness:54-57 HRC.

Tempering:

In the range 550-630°C for 4-6 hours according to the hardness required, the dimensions of the parts and preating conditions, cooling in still air.

Before tempering, preheat the parts to 200-300°C.

,based on the over one hundred years’s production history of in Huangshi, provide professional services and material for cutting tool companies, mould companies and other industrial enterprises all over the world for years.

Другие товары поставщика

	High toughness H13 1.2344 SKD61 Hot Work Tool Steel	Product Details Chemical Composition (%) Standard Steel Grade C Si Mn P S Cr Mo V W DIN -　 ASTM H13 ...
	H11/1.2343 Hot Work Tool Steel Following NADCA standard	Product Details Chemical Composition (%) Standard Steel Grade C Si Mn P S Cr Mo V W DIN -　 ASTM H11 ...
	M2/1.3343 High Speed Tool Steel Plates/Bars/Sheet /Forgings	Molybdenum high speed tool steel. Very high resistance to softening at elevated temperatures. Very high resistance to wear. Good toughness and cut...
	45CrNi4Mo/1.2767 Hot Work Tool Steel Plates Bars Sheet Forgings	Product Details Chemical composition C Mn Si Cr V Mo P S - ≤0.03 ≤0.03 Equivalent grades: DIN AFNO...
	D3/1.2080 Cold Work Tool Steel Plates Bars Sheet Forgings	Commonly used for manufacturing cold work moulds of excellent abrasion resistance with light shock loads, punch heads, cold cutting scissors, dril...

Все товары поставщика

Похожие товары

	Прямая труба из хромоникелевого сплава центробежного литья	Продавец: Нанкин Xinshuo Механическое оборудование Лтд	Прямая труба из хромоникелевого сплава центробежного литьяДля получения дополнительной техническо...
	White Iron Wear Blocks, Wear Bars	Продавец: Yiwu WALKSON Machinery Equipment Co., Ltd.	The unique, formable designed wear bars is available in various lengths, grades and sizes and can...
	TITANIUM ALLOY STEEL TUBE	Продавец: YUHONG GROUP CO., LIMITED ZHEJIANG YUHONGWELL STEEL CO., LIMITED	TITANIUM ALLOY STEEL TUBE Titanium is the ninth most abundant element in the earth's crust and t...
	STEEL FITTING	Продавец: YUHONG GROUP CO., LIMITED ZHEJIANG YUHONGWELL STEEL CO., LIMITED	STEEL FITTING Steel has been used for making pipe and pipe fittings for years for its durability...
	STAINLESS STEEL PIPE/TUBE	Продавец: YUHONG GROUP CO., LIMITED ZHEJIANG YUHONGWELL STEEL CO., LIMITED	STAINLESS STEEL PIPE/TUBE Stainless steel pipe/tube is one of the most widely used in manufactur...