Color PEEK R&D Series
PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw material. Having good thermal stability, color consistency, high purity, and high-temperature resistance, our PEEK material colorR&D series is just as high quality as other naturalPEEK materialseries.
PEEK Material Color R&D Series Specifications
|
Material Properties |
Test Method |
Conditions |
Units |
770G |
|
Mechanical Data |
||||
|
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
100 |
||
|
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
|
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
|
Y ield,23℃ |
MPa |
165 |
||
|
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
|
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
|
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
|
Across flow |
% |
|||
|
Thermal Data |
||||
|
Melting Point |
ISO 11357 |
℃ |
343 |
|
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
|
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
|
Along flow above Tg |
ppm K-1 |
120 |
||
|
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
|
Flow |
||||
|
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
|
Miscellaneous |
||||
|
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
|
Amorphous |
gcm-3 |
|||
|
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
|
by immersion |
Equilib riu m,23℃ |
% |
||
|
Electrical Data |
||||
|
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
|
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
|
23℃,50kHz |
3 |
|||
|
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
|
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
|
275℃ |
Ω cm |
10 9 |
||
More types of peek composite material, please visit our website.
Send product request
Other supplier products
|
|
Color PEEK R&D Series | PEEK ColorR&D Series can be customized according to the customer's own demand. Different PEEK plastic colorscan be chosen for our PEEK raw mate... |
 |
Grade FC Super Wear Resistant PEEK | PEEK-FC series modified by PTFE, graphite and carbon fiber have lower friction coefficient, wear resistance and self-lubrication than pure resin G.... |
 |
Grade PF PEEK Pure Resin Fine Powder | The material is obtained by grinding the coarse powder (D50 is 13 micron ~ 75 microns) . It can be used as moulding material, spraying material and... |
 |
Peek in Bearing Material | Peek in Bearing Material Due to its excellent mechanical strength, dynamic fatigue resistance, high-temperature resistance, creep resistance, se... |
 |
Peek Tube Material | Peek Tube Material Peek plastic materialhas great machinability, excellent dimensional stability, high-temperature resistance, creep resistance ... |