Fluxes for Aluminum Alloy
General Description:
Aluminum alloys containing more than 2 % magnesium become brittle with sodium.
Feature: This flux is a compact covering and cleaning granulated flux to remove the sodium in the aluminum melting. It generates low dust and low fume during application. It reacts quickly with molten aluminum and removes the alkali metal (Ca, Na, Li, Sr) and non-metallic inclusions (oxides, carbides, borides) and degassing.
Function:
After fusing completed the flux are cooled and they are crushed or ground into ccustomerized particle size.
degassing when injected flux with Argon or Nitrogen.
Applied range:
This flux is used in hypo-eutectic aluminum alloys including those contain high magnesium alloy.
Chemical compositions
Mgcl2 Anhydrous , Potassium Chloride , CaF2 and other salt
Melting Point: 432°C & 483°C
Size of Sodium-Free Refining Flux
Granule 0.8-3.25mm, 1-3mm,Other size can be adjusted according to custom
Package: 1. 2.0kg or 2.5kg or 5kg heat sealed polyethylene (PE) bags into 20 or 25kgs bags or cartons with or without pallet
Advantage:
1) Eco‐friendly flux that reduce dust levels, meet the emission limits of most environmental regulatory agencies
2) Uniform size, reacts fully. Purify the melt improve melt quality.
3) Increases the extrusion speed and die life when extruding profiles
4) Reduces the number of breaks in continuous casting
5) Eliminates edge cracks when rolling high Mg aluminium alloys
6) Free of fluorides. Zero fluoride emissions.
7) Low melting point for rapid dispersion
8) Low application rates, typical 0.15-0.2% of MT aluminium
Notice:
Sodium-free flux should be added to the melt at the temperature of 690-750 Degree Celcius. The recommended application rate should be 0.1 to 0.2% of the melt size. Rebel the melt and remove the dross from the top of the molten metal.
Send product request
Other supplier products
 |
Covering Flux | General Introduction: Chemical formular: Mgcl2 6H2O Purity: 46.00%min. Appearance: pure white crystal power CAS NO.:7791-18-6 Chemically, is repr... |
 |
Drossing Flux | Drossing Flux(SATA-PF-310) Description of Drossing Flux (SATA-PF-310) SATA drossing flux also name aluminum drossing fluxis specially developed for... |
 |
Powder Refining Flux | Powder Refining Flux (SATA-PF-330) General Description of Powder Refining Flux (SATA-PF-330) For aluminium alloys, since the Al has strong chemical... |
 |
Master Alloy | Master AlloyManufacturer Description of Master Alloy SATA-Master alloys melt at a lower temperature as compared to primary metals. Controlled addit... |
 |
Sodium-Free Refining Flux | General Description: Aluminum alloys containing more than 2 % magnesium become brittle with sodium. Feature: This is a compact covering and cleanin... |