CA Series-330CA30 PEEK Carbon Fiber Reinforcement
CA Series-330CA30 PEEKFC, CFPEEKcarbon fiber reinforcement is suitable for the production of bushing seals and other products, can be faster from the bearing surface heat dissipation, at the same time has a high thermal deformation temperature (336 ° C) , also can maintain strength at high temperature, to a certain extent, can replace metal materials.
Specification of CA Series-330CA30 PolyetheretherketoneCarbon Fiber Reinforcement
Material Properties |
Test Method |
Conditions |
Units |
770G |
Mechanical Data |
||||
Tensile Strength |
ISO 527 |
B reak,23℃ |
MPa |
- |
Y ield,23℃ |
MPa |
100 |
||
Tensile Elogation |
ISO 527 |
Break,23℃ |
% |
45 |
Flexural Strength |
ISO 178 |
Break,23℃ |
MPa |
- |
Y ield,23℃ |
MPa |
165 |
||
Fleoural Modulus |
ISO 178 |
23℃ |
Gpa |
|
Compressive Strength |
ISO 604 |
23℃ |
MPa |
125 |
Charpy Impact Strength |
ISO 179/leA |
Notched |
kJm-2 |
7 |
ISO 179/IU |
Unnotched |
kJm-2 |
- |
|
Izod Impact Strength |
ISO 180/A |
Notched |
kJm-2 |
|
ISO 180/U |
Unnotched |
kJm-2 |
- |
|
Mould Shrinkage |
ISO 294-4 |
Along flow |
% |
1 |
Across flow |
% |
|||
Thermal Data |
||||
Melting Point |
ISO 11357 |
℃ |
343 |
|
Glass Tansition (Tg) |
ISO 11357 |
Onset |
℃ |
143 |
Special Heat Capacity |
DSC |
23℃ |
kj kg-1℃-1 |
|
Coefficient of Thermal Expansion |
ISO 11359 |
Along flow below Tg |
ppm K-1 |
45 |
Along flow above Tg |
ppm K-1 |
120 |
||
Heat Deflecion Temperature |
ISO 75A-f |
℃ |
152 |
|
Thermal Conductivity |
ASTM C177 |
23℃ |
W m-1K-1 |
|
Flow |
||||
MeltIndex |
ISO 1133 |
380℃,5kg |
g10min-1 |
10 |
Miscellaneous |
||||
Density |
ISO 1186 |
Crystalline |
gcm-3 |
|
Amorphous |
gcm-3 |
|||
Shore D Hardness |
ISO 868 |
23℃ |
85 |
|
Water Absorption(3.2mm thick Tensile Bar) |
ISO 62-1 |
24h,23℃ |
% |
|
by immersion |
Equilib riu m,23℃ |
% |
||
Electrical Data |
||||
Dielectric Strength |
IEC 60243-1 |
2mm |
kV mm-1 |
23 |
Comparative Tracking Index |
IEC 60112 |
V |
150 |
|
Dielectric Constant |
IEC 60250 |
23℃,1kHz |
||
23℃,50kHz |
3 |
|||
Loss Tangent |
IEC 60250 |
23℃,1MHz |
||
Volume Resistivity |
IEC 60093 |
23℃,1V |
Ω cm |
10 16 |
275℃ |
Ω cm |
10 9 |
As one of peek suppliers, we will do our best to meet all the needs of customers.
在线联系供应商
Other supplier products
CA Series-550CA30 PEEK Carbon Fiber Reinforcement | CA Series-550CA30peek carbon fiberreinforcement is a 30% carbon fiber reinforced naturalPEEK material, the addition of carbon fiber significantly i... | |
Grade PF PEEK Pure Resin Fine Powder | The material is obtained by grinding the coarse powder (D50 is 13 micron ~ 75 microns) . It can be used as moulding material, spraying material and... | |
Dental Tooth Materials PEEK R&D Series | PEEKTeethR&D Series has good wear resistance and high mechanical strength. It is mainly used in dentistry in medical field. Specification of... | |
Grade PF PEEK Pure Resin Fine Powder | The material is obtained by grinding the coarse powder (D50 is 13 micron ~ 75 microns). It can be used as moulding material, spraying material and ... | |
Peek Tube Material | Peek Tube Material Peek plastic materialhas great machinability, excellent dimensional stability, high-temperature resistance, creep resistance ... |
Same products
LUBE SH-ONE-4S 400G for Fanuc Machines | 卖方: 广东聚广恒自动化设备有限公司 | TheSH-ONEseries ofgreaseisoneof the latest released byLUBEand are used on a range of Fanuc machines | |
Mobil Grease 28 Synthetic Aviation Grease | 卖方: 广东聚广恒自动化设备有限公司 | Mobilgrease 28is the polyalphaolefin (PAO), clay-based multipurpose airframe and wheel bearing gr... | |
Kluber Isoflex Topas NCA 5051 50ml Original Lubricants | 卖方: 广东聚广恒自动化设备有限公司 | ISOFLEX TOPAS NCA 5051 is used in plain bearings in the automotive industry. ISOFLEX TOPAS NCA 50... | |
CHRISTO-LUBE MCG 111 2-OZ Valve Seal Grease | 卖方: 广东聚广恒自动化设备有限公司 | CHRISTO-LUBE®MCG 111Oxygen Compatible Grease is designed to protect components against extrem... | |
Permatex 81160 85G High Temperature Resistant Resin | 卖方: 广东聚广恒自动化设备有限公司 | PermatexHi-Temp RED RTV Silicone Gasket is designed to provide reliable “formed-in-place&rd... |