Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
During the processing of bearing rings, various defects are often generated on the surface or inside, andcrack testing equipmentoccupy a large proportion of all defects.
The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ferrules, if the process is not proper, the cracks may be directly caused or the hidden cracks may be buried for the occurrence of the lap ring grinding cracks.
There are many ways to form cracks in bearing rings: Raw material defects include: cracks in raw materials and the effects of raw material defects on the grinding process.
Forging defects include forging cracks, effects of forged microstructure defects on the grinding process, and cutter cracks. There are also various heat treatment defects and the like. Therefore, crack detection and hardness testing are essential. BKNhas considerable experience in crack detection, and Bearing Ring Crack and Hardness Combination testing equipment is a perfect combination.
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 Brief Introduction
Detection process
Vibrating plate and string charging →hardness test→crack detection→automatic blanking
↓
Bad product sorting
Automatic charging —automatic detection—automatic sorting —automatic blanking
Crack sensitivity: a crack with a depth of ≥0.05 mm and a length of ≥1 mm extending inward from the surface of the ferrule; for a crack that has not extended to the surface inside the ferrule, when the thickness between the subcutaneous surface and the surface of the workpiece is ≤0.2 mm, the depth is ≥0.20 mm Cracks of length ≥ 1 mm can be detected.
Hardness sensitivity: Rockwell 1HRC ~ 2HRC (other parameters remain stable and consistent).
Nanjing BKN Automation System Co., Ltd. is an non destructive testing equipment manufacturersand has long been committed to the development and production of bearing hardness and crack eddy current screening equipment.
在线联系供应商
Other supplier products
 |
Eddy Current Testing Equipment | ECT Eddy current testing used by eddy current test setis a non-contact testing method, which mainly uses the electromagnetic field and electromagne... |
 |
GSET-551 Steel Wire Eddy Current Flaw Detector | GSET-551 Steel Wire Eddy Current Flaw Detector GSET-551 Steel Wire Eddy Current Flaw Detector Brief Introduction Using the eddy current signa... |
 |
EDM Notch | An electric pulse is a pulse generated by electrons, and a pulse is a process of changing a voltage in a short time. Electropulsing is an unsteady ... |
 |
Steel Bar Testing | The steel bar is rolled by a rolling mill and produce both surface defects and internal defects during the rolling process. The internal defect is ... |
 |
MFL101 Tank Floor MFL Scanner | Technical Characteristics ofMFL101 Tank Floor MFL Scanner Unique full modular structure, from the main body of the computer mechanism the handle o... |
Same products
 |
C500-1.7 Series High Flow Multi-Stage Centrifugal Blower /Centrifugal Blower | 卖方: Greentech International (Zhangqiu) Co., Ltd | Greentech International (Zhangqiu) Co., Ltdis the professional blower supplier.Multistage Centrif... |
 |
Common Rail injector control valve F00VC01303 | 卖方: China Lutong Part Plant | Common Rail injector control valve F00VC01303 Tina#Stainless Steel Cylindrical Pin##Denso Common... |
 |
Common Rail injector control valve F00VC01200 | 卖方: China Lutong Part Plant | Common Rail injector control valve F00VC01200 Tina#Stainless Steel Cylindrical Pin##Denso Common... |
 |
Injector Control Valve Plate 24# | 卖方: China Lutong Part Plant | Injector Control Valve Plate 24# Tina#Stainless Steel Cylindrical Pin##Denso Common Rail Injecto... |
 |
Injector Control Valve Plate 12# | 卖方: China Lutong Part Plant | Injector Control Valve Plate 12# Tina#Stainless Steel Cylindrical Pin##Denso Common Rail Injecto... |