PA6 GF30 Halogenated FR (A1014F) for Engineering Plastics
PA6 GF30 FRis a PA6 with 30% glass-fibers and halogens flame retardant.
PA 6 GF30Halogenated FR Features
|
Glass fiber reinforced 30% |
PA66 |
PA6 |
|
Density(g/cm3) |
||
|
Water absorption(%) |
1 |
|
|
Surface hardness |
M100 |
M100 |
|
Shrinkage(%) |
||
|
Continuous heat resistance |
82-148 |
93-148 |
|
Heat distortion temperature(1.82MPa) |
252 |
210 |
|
Heat distortion temperature(0.45MPa) |
257 |
221 |
|
Tensile Strength/Mpa |
||
|
Elongation(%) |
3~5 |
5 |
|
Flexural yield strength/Mpa |
||
|
Flexural modulus of elasticity/Mpa |
||
|
Compressive strength/Mpa |
||
|
Izod notched impact strength/(J/m) |
||
|
Melting point/°C |
264 |
220 |
|
Decomposition temperature/°C |
360 |
320 |
|
Drying temperature/°C |
100 |
100 |
|
Drying time/h |
3~5 |
3~5 |
|
Injection temperature/°C |
240~280 |
240~280 |
|
Mold temperature/°C |
40~90 |
40~90 |
PA6 GF30 PlasticHalogenated FR Description
Halogen-free flame retardant nylon PA6 GF30 granule have the properties of low flame retardant density, low product shrinkage, excellent electrification performance, and less corrosion to molds.
- Flame retardant grade UL94-V0.
It meets glow-wire ignition temperature (GWIT) testing demands, recording as:
GWFI：750/3.0 （Note：750℃=725℃+25℃）
GWFI：850/3.0
-Compliant with ROHS standard
PA6 GF30 is used in connectors of baby stroller, auto parts, power tool housings and mechanical parts, etc.With the rapid development of new energy vehicles (including hybrid, pure electric and hydrogen energy), the automotive industry has an increasing demand for light weight, integration, miniaturization and electrification of auto parts. Nylon6 has a unique role and development prospects in the manufacture of integrated components for new energy vehicles.
PA6 GF30 halogenated FR (A1014F) Typical Application
PA6 GF30 flame retardant has achieved full coverage from electronic & electrical fields to the industrial, commodity consumer market, and even the automotive industry. Such as MCB panel (v0), power tool housing (HB), small household appliance accessories for bread machine housing and vacuum cleaner accessories (HB), and daily necessities structural parts-office chair legs (HB) and exhaust duct (HB), etc.
PA6 PA6 GF30 halogenated FR (A1014F) Other Details
Physical Property
|
Ash |
(15.0% 1 ISO3451/1) |
|
Conditioned |
600°C*2h |
|
Density |
(1250Kg/m3 1 ISO1183) |
|
Conditioned |
23°C |
|
Shrinkage Parallel Flow |
(0.5-0.7 % 1 ISO294-4) |
|
Shrinkage Vertical Flow |
(0.7-1.1% I ISO294-4) |
Mechanical Properties
|
Tensile strength(125.0MPa 1 ISO527) Conditioned |
5mm/ min |
|
Tensile Strain at Break(2.5% I ISO527) Conditioned |
|
|
Notched Impact Strength(125 0MPa I ISO527) Conditioned |
2mm/min |
|
Flexural Strength(190MPa 1ISO178) Conditioned |
2mm/min |
|
Flexural Modulus(5700 MPa I ISO178) Conditioned |
5mm/ min |
Thermal Property
|
Melting Point |
(220°C I ISO11357) |
|
Hot Deformation Temperature |
(175*C I ISO75) |
|
Conditioned |
|
|
Flammability Class |
(HB 1UL94) |
|
Conditioned |
mm |
Injection Molding Conditions
|
Drying Temperature |
130°C |
|
Drying Time |
3h |
|
Cylinder Temperature |
240-260°C |
|
Nozzle Temperature |
240-260*C |
|
Tooling Temperature |
80*C |
* Molding conditions arejustfor reference, please make an adjustment based on the actual situation！
If you want to know more about PA6 GF30 properties, please visit our website.
As one of masterbatch suppliers, we can offer sorts of related products for sale, is you have needs to buy masterbatch, please leave us a message.
在线联系供应商
Other supplier products
 |
Low-shrinkage PBT Masterbatch for Engineering Plastics | Tubes are colored to make the identification process easier in loose tube optical fiber cables. Low-shrinkage PBT masterbatchmaterial as loose tube... |
 |
Nylon66 PA66 Halogen-free FR (A2005X01) for Engineering Plastics | Nylon66 PA66FRHalogen-free FR (A2005X01) for Engineering Plastics Flame-retardant PA66 is a halogen-free flame retardant engineering plastic made ... |
 |
Antibacterial Masterbatch for Engineering Plastics | Polymer anti-bacterial masterbatch is a kind of masterbatch materialthat adds antibacterial agents into the carrier resin, which is offering antimi... |
 |
PA66 GF30 Heat Stabilized (A2006F, A2016F) for Engineering Plastics | Polyamide 66, reinforced with 30% of glass fiber, heat stabilized, for injection moulding. Typical Application of pa6 6 gf30Heat Stabilized (A2006... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | PA66 GF15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection molding. PA66 GF15 Storage and Handling PRE-PROCESS... |
Same products
 |
Medical Plastic Parts | 卖方: Packson Mold Co.,Ltd | Project Management To be a qualified medical plastic components manufacturer, the most advanced ... |
 |
PA66 GF15 Heat Stabilized (A2006C, A2016C) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | PA 66 GF 15is a 15% glass fiber reinforced, heat-resistance, polyamide 66 resin for injection mol... |
 |
PA66 GF | 卖方: Suzhou Anmei Material Technology Co., Ltd | Anmei focuses on the production of modified engineering plastics. We have polyamide pa6 6gfmodif... |
 |
Nylon6 PA6 | 卖方: Suzhou Anmei Material Technology Co., Ltd | Other than fiber-reinforced pa6 polyamide, the unreinforced nylon type 6 produced by Anmei, one o... |
 |
Nylon 66 Pa66 With High Tensile Strength (A2307X01, A2317X01) for Engineering Plastics | 卖方: Suzhou Anmei Material Technology Co., Ltd | Using Polyamide 66 as the basic resin, the tensile strength of nylon 66 is obtained by blending a... |