AKRON abrasion testing machine
Product Introduction
AKRON wear testing machine is used with the balance, specially testing the wear resistance of rubber products such as soles, tires, car tracks, etc. The counters are electronic automatic, which can set the wear revolution, and automatically stop when the set revolution is reached.
Standard
GB/T 1689 standard, ISO:4661-1:1993. ISO 2481:1988. ISO 471:1983. ISO 1826:1981
Test size
Outer diameter 2 ", inner diameter 1/2 ", thickness 1/2 ", circumference 220mm, hardness 60——70
Machine operation method
1. Prepare the core of the specimen according to the conditions of obtaining the specimen. And record its exact weight.
2. Fix the specimen core on the core shaft seat, and then adjust the Angle of the specimen. (Usually set to 15∘)
3. Different test methods are divided into high standards and low standards according to material requirements.
3.1 High standard requirements:
a. Angle (the Angle between the test piece and the grinding wheel)15∘
b. Load :6 pounds
c. Pre-grinding revolutions :300 revolutions
d. Remove the specimen core, brush with a clean brush to remove the powder, then weigh the exact weight with a precision balance, and record the weight of the sample before the test
e. Install the specimen core and set the wheel rotation times :3000 revolutions
f. After the wear is completed, remove the specimen, brush with a clean brush to remove the powder, and then weigh the accurate weight with a precision balance, which is the weight of the sample after the test
g. Substitute the formula to calculate the grinding amount
3.2 Low standard requirements:
a. Angle (the Angle between the test piece and the grinding wheel)15∘
b. Load :2 pounds
c. Pre-grinding revolutions :200 revolutions
d. Remove the specimen core, brush with a clean brush to remove the powder, then weigh the exact weight with a precision balance, and record the weight of the sample before the test
e. Load back the specimen core and set the wheel rotation times :2000 revolutions
f. After wearing, remove the specimen, brush with a clean brush to remove the powder, and then weigh the exact weight with a precision balance
This is the test weight after the test
g. Substitute the formula to calculate the grinding amount
4. After all specimens have been tested, remove the weight and store it, and remove the debris on the machine.
Wear value calculation method:
Wear (volume m1)== Weight before test - weight after test
Specific gravity algorithm:
a. If the test material is heavier than water
Specific gravity = Weight in air ÷(weight in air - weight of sample in water)
b. If the test material is lighter than water
Specific gravity = weight in air ÷ volume
Technical parameters
Grinding wheel diameter Φ150mm, 40mm(w)， particle size 36#
Grinding wheel speed 34±1r/min
The incline range of the test material is adjustable from 0 to 35°
Test shaft speed (GB)76±2r/min
Load 26.7N±0.2
Counter LED, 0——99.999.999
Volume (W×D×H) 60 × 50 × 45cm
Weight (approx) 60 kg
Power 1 #,AC220V, 50Hz (depending on country or designation)
在线联系供应商
Other supplier products
 |
Nissan Scratch Tester-QINSUN | Standard ASTM D7027(Standard Test Method for Scratch Resistance of Polymeric Coatings and Plastics) ISO 1518(Paints and Varnishes — Determi... |
 |
Leather Seam Fatigue Tester | Standards ISO 5402: Leather physical testing – Flex tester method for adhesion and strength analysis. SATRA TM55: Seam fatigue testing fo... |
 |
Scratch Resistance Tester | Product Introduction: The Scratch 5.5 Machine is a scratch and scratch test instrument for macroscopic scratches. It is a research-grade tribology... |
 |
Textile Far - Infrared Radiation Heating Tester | Application ScopeThis instrument is used to determine the far-infrared properties of various textile products, including fibers, yarns, fabrics, no... |
 |
Automotive wire cyclic bending testing machine | Standard This testing machine aligns with global automotive industry standards for wire harness reliability, includingISO 6722(Road vehicles &ndas... |
Same products
 |
HDPE高速水冷双壁波纹管生产线 | 卖方: Shandong HUASU Plastic Technology Co.,Ltd. | 机头模具采用双流道结构、氮化磨光处理机头，偏壁调整方便快捷，保证内外层壁厚均匀和稳定成型。 最新设计密闭压力水冷冷却结构，冷却充分，多点分布真空系统，效率更高，生产速度更快。 双层在线扩口功... |
 |
PanEVAP & MVR system | 卖方: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd | A multiple-effect evaporator is a device that efficiently uses steam heat to evaporate water. Wat... |
 |
PanGAP wide gap welded plate heat exchanger | 卖方: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd | PanGAP wide gap welded plate heat exchangerconsists of a welded plate pack with different channel... |
 |
PanBloc welded plate heat exchanger | 卖方: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd | PanBloc welded plate heat exchangeris compact and efficient, although fully welded, is totally ac... |
 |
PanBox welded plate heat exchanger | 卖方: Yangzhou Panstar Heat Exchanger Equipment Co., Ltd | PanBox welded plate heat exchangerconsists of a laser welded plate pack with optimized corrugated... |