Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02

The technology of BKN originated from eddy current Laboratory of Institute of Materials, Nanjing University of Technology. At present, it is a leading high-tech enterprise specializing in developing types of NDT non-destructive testing instruments and equipment in China. As one of the non destructive testing equipment suppliers, the company is committed to the development of eddy current, ultrasonic, magnetic flux leakage and various non-standard equipment, holding independent research and development of a number of national patents.

During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all defects.

The cause of the cracks in the bearing rings is complicated. From the raw materials to the finished products of the ferrules, if the process is not proper, the cracks may be directly caused or the hidden cracks may be buried for the occurrence of the lap ring grinding cracks.

There are many ways to form cracks in bearing rings: Raw material defects include: cracks in raw materials and the effects of raw material defects on the grinding process.

Forging defects include forging cracks, effects of forged microstructure defects on the grinding process, and cutter cracks. There are also various heat treatment defects and the like. Therefore, crack testing equipmentand hardness testing are essential. BKNhas considerable experience in crack detection, and Bearing Ring Crack and Hardness Combination testing equipment is a perfect combination.

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 Brief Introduction

Detection process

Vibrating plate and string charging →hardness test→crack detection→automatic blanking

Bad product sorting

Automatic charging —automatic detection—automatic sorting —automatic blanking

Crack detection(the probe uses stainless steel casing+nano abrasion material ) to ensure long-term normal of the probe

Crack sensitivity: a crack with a depth of ≥0.05 mm and a length of ≥1 mm extending inward from the surface of the ferrule; for a crack that has not extended to the surface inside the ferrule, when the thickness between the subcutaneous surface and the surface of the workpiece is ≤0.2 mm, the depth is ≥0.20 mm Cracks of length ≥ 1 mm can be detected.

Hardness sensitivity: Rockwell 1HRC ~ 2HRC (other parameters remain stable and consistent).



在线联系供应商

至: Nanjing BKN Automation System Co.,LTD
Your E-mail:
消息正文:


Send to other suppliers

Other supplier products

Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02
Bearing Ring Crack and Hardness Combination Flaw Detector TQJC-02 During the processing of bearing rings, various defects are often generated on the surface or inside, and cracks occupy a large proportion of all d...
Steel Bar Testing
Steel Bar Testing The steel bar is rolled by a rolling mill and produce both surface defects and internal defects during the rolling process. The internal defect is ...
Bolt Eddy Current Sorter BKNFX-11
Bolt Eddy Current Sorter BKNFX-11 The technology of BKNoriginated from eddy current Laboratory of Institute of Materials, Nanjing University of Technology. At present, it is a leadi...
BKNET-0102 Welded Pipe Eddy Current Flaw Detector
BKNET-0102 Welded Pipe Eddy Current Flaw Detector Eddy current weld testingis the use of eddy current technology to test the welded pipe, this type of testing is based on the premise of lossless. A...
Portable Magnetic Flux Leakage Testing Equipment
Portable Magnetic Flux Leakage Testing Equipment Magnetic flux leakage test refers to the formation of a leakage magnetic field on the surface of a test piece after it is magnetized due to defects...
供应产品

Same products

H2500R-2 4x1000mL High Speed Refrigerated Centrifuge
H2500R-2 4x1000mL High Speed Refrigerated Centrifuge 卖方: Hunan Xiang Yi Laboratory Instrument Development Co., Ltd. H2500R-2 Large Capacity High Speed centrifugation in chemistry H2500R-2 high speed refrigerate...
H2100R 4x750mL High Speed Refrigerated Centrifuge
H2100R 4x750mL High Speed Refrigerated Centrifuge 卖方: Hunan Xiang Yi Laboratory Instrument Development Co., Ltd. H2100R Benchtop Large Capacity High Speed Refrigerated Centrifuge Model H2100R is an advanced ...
H2050R 4x750mL High Speed Refrigerated Centrifuge
H2050R 4x750mL High Speed Refrigerated Centrifuge 卖方: Hunan Xiang Yi Laboratory Instrument Development Co., Ltd. H2050R Benchtop Large-Capacity High Speed Refrigerated Centrifuge 12 kinds of rotors are avail...
H2050R-1 4x750mL High Speed Refrigerated Centrifuge
H2050R-1 4x750mL High Speed Refrigerated Centrifuge 卖方: Hunan Xiang Yi Laboratory Instrument Development Co., Ltd. H2050R-1 Large-Capacity High Speed Refrigerated Centrifuge 12 kinds of rotors are available fo...
H1850 4x100mL High Speed Centrifuge
H1850 4x100mL High Speed Centrifuge 卖方: Hunan Xiang Yi Laboratory Instrument Development Co., Ltd. H1850 Benchtop High Centrifuge 15 rotors and many kinds of adapters are available for H1850. 6...